Persistent luminescence (PersL), also called long-lasting phosphorescence or simply afterglow, is a luminescence characterised by the emission of radiation from a few seconds to several days after the excitation source has been switched off. Over the past two decades, research on PersL materials, both in fundamental and applied physics, has developed rapidly; however, the explanation for the physical processes that cause afterglow still needs to be clarified. Today, PersL materials are used mainly for luminescent paints, safety signs and decorations. At the same time, research into using such materials in medicine, information storage, anti-counterfeiting technology, etc., is underway.
Currently, information on the long persistent luminescence materials with emission in the blue and green spectral range is widely available. In contrast, the number of publications on the afterglow in the red and near-infrared spectral range is considerably lower.
Within the framework of this research, Mg2SiO4: Mn2+; M3+ (M3+ = B3+; Al3+; Ga3+; In3+) materials were synthesised using solid state reaction synthesis. When excited with X-rays, the materials exhibited a broad Mn2+ PersL band with two maxima at approximately 625 nm and 730 nm. After cessation of irradiation, an afterglow of at least 6 hours could be observed.
The research focuses on the trap properties of the materials. It was concluded that at least three discrete trap levels with activation energies approximately between 0.4–1.6 eV were present in the samples. Additionally, co-doping with Al3+; Ga3+; In3+ ions improved PersL longevity of the Mg2SiO4: Mn2+ material.
</abstract>

Persistent luminescence (PersL), also called long-lasting phosphorescence or simply afterglow, is a luminescence characterised by the emission of radiation from a few seconds to several days after the excitation source has been switched off. Over the past two decades, research on PersL materials, both in fundamental and applied physics, has developed rapidly; however, the explanation for the physical processes that cause afterglow still needs to be clarified. Today, PersL materials are used mainly for luminescent paints, safety signs and decorations. At the same time, research into using such materials in medicine, information storage, anti-counterfeiting technology, etc., is underway.
Currently, information on the long persistent luminescence materials with emission in the blue and green spectral range is widely available. In contrast, the number of publications on the afterglow in the red and near-infrared spectral range is considerably lower.
Within the framework of this research, Mg2SiO4: Mn2+; M3+ (M3+ = B3+; Al3+; Ga3+; In3+) materials were synthesised using solid state reaction synthesis. When excited with X-rays, the materials exhibited a broad Mn2+ PersL band with two maxima at approximately 625 nm and 730 nm. After cessation of irradiation, an afterglow of at least 6 hours could be observed.
The research focuses on the trap properties of the materials. It was concluded that at least three discrete trap levels with activation energies approximately between 0.4–1.6 eV were present in the samples. Additionally, co-doping with Al3+; Ga3+; In3+ ions improved PersL longevity of the Mg2SiO4: Mn2+ material.

Red Persistent Luminescence and Trap Properties of Mg2SiO4: Mn2+, M3+ (M3+ = B3+; Al3+; Ga3+; In3+) Material

Latvian Journal of Physics and Technical Sciences

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Red Persistent Luminescence and Trap Properties of MgSiO: Mn, M (M = B; Al; Ga; In) Material

Persistent luminescence (PersL), also called long-lasting phosphorescence or simply afterglow, is a luminescence characterised by the emission of radiation...

Red Persistent Luminescence and Trap Properties of Mg₂SiO₄: Mn²⁺, M³⁺ (M³⁺ = B³⁺; Al³⁺; Ga³⁺; In³⁺) Material

Publicado en línea: 30 mar 2024

Páginas: 3 - 12

DOI: https://doi.org/10.2478/lpts-2024-0008

Palabras clave
Activation energy, Mn, persistent luminescence, thermally stimulated luminescence, traps

© 2024 G. Doke, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Red Persistent Luminescence and Trap Properties of Mg2SiO4: Mn2+, M3+ (M3+ = B3+; Al3+; Ga3+; In3+) Material

Publicado en línea: 30 mar 2024

Páginas: 3 - 12

DOI: https://doi.org/10.2478/lpts-2024-0008

Palabras claveActivation energy, Mn, persistent luminescence, thermally stimulated luminescence, traps

© 2024 G. Doke, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Red Persistent Luminescence and Trap Properties of Mg₂SiO₄: Mn²⁺, M³⁺ (M³⁺ = B³⁺; Al³⁺; Ga³⁺; In³⁺) Material

Palabras clave
Activation energy, Mn, persistent luminescence, thermally stimulated luminescence, traps