This paper is focused on the problematics of weld joint corrosive degradation in the boiler water environment. The boiler water is commonly used in power industry. The corrosion experiment simulated the boiler water environment during shutdown, when chemicals may be concentrated in the deposits, or as a result of evaporation. The corrosion experiment was performed on heterogeneous weldments made of P265GH//X6CrNiTi18-9 steels in the environment of stagnant boiler water with the addition of NaCl for 53 days. The data showed only minimal weight losses, and small changes in the measured fracture toughness of the welded joint. At the same time, a tendency for a mechanical weakening of the welded joint with the increasing aggressivity of the boiler water environment was observed. The metallographic analysis was performed to describe the nature of corrosive degradation.
Defects on silver based coatings Growth kinetics of diiron boride (Fe2B) layer on a carbon steel by four approaches Corrosion and tribological behaviour of Friction Stir Processed AA2024-T351 alloy Metal Antik conservation coatings on iron specimens Corrosion assessment of a bronze equestrian statue exposed to urban environment Experimental assessment of packaging paper properties effect in combination with storage conditions on the adhesion performance of automotive glass Innovative accident tolerant nuclear fuel materials will help extending the life of light water reactors Prediction models for the kinetics of iron boride layers on AISI 316L steel Resistance of the welded joint of austenitic steel NEUTRONIT A 976 SM in the corrosive environment of boric acid Impact of the diffusion coefficient calculation on predicting Fe2B boride layer thickness Experimental studies on the corrosion inhibition of mild steel by 1-(phenylamino-1,3,4-thiadiazol-5-yl)-3-phenyl-3-oxopropan complemented with DFT Modeling Dissimilar weld joint corrosion in simulated boiler water environment