The extensile mesh reflector of an antenna consists of fine wires with a low thermal expansion coefficient and high resistance to UV. A functional coating with good electrical properties, with a base of gold, silver, rhodium or organic materials like polyurethane, is added to these fine wires [1]. Nickel-plated stainless steel wire is normally used for low-frequency (LF) antennas, and gold-plated molybdenum for high-frequency (HF) ones [2]. Therefore, compared with conventional fabric, warp-knitted mesh-like antennas show significantly different performances, because of the high-performance metallic yarns used as raw material.
As one of the high-performance fibers, the metallic yarn knitting process is quite different from that of conventional yarns. Firstly, high strength of the yarn only appear in the axial direction, even if it has a high-performance fibers composition [3]. These fibers’ low surface strain, high tensile set and low out-of-plane properties bring difficulties to the knitting process [4]. Secondly, high-performance fibers cannot not be knitted smoothly due to the high-tension peaks resulting from low elongation. While garment fibers with elastic elongation can be processed easily [5-6]. Thirdly, part of these fibers is easily broken under extremely lower loads than that that which leads to elongation breakage, because yarns are subjected to pressure from bending, and sometimes even from both bending and stretching in the knitting process [7-9]. Generally, the performance of yarn in the knitting process, i.e. whether the yarn can be knitted smoothly, is called knittability [10]. The knittability of yarns is hard to characterise and measure directly [11]. Therefore, methods for the quantitative characterization of knittability should be investigated.
The current study mainly concentrated on fiber damage, simulation testing and fiber performance measurement for knittability characterization. However, these methods were still not clear or accurate. The yarn strength loss in knitted fabric can be quantitatively characterized for yarn knittability, but only for disassembled fabric [11]. In this study, the ratio of predicted tensile properties of single yarn inside warp-knitted fabrics to that of the original one, called the knitted yarn strength utilization factor, was used for characterizing knittability. Furthermore, the method extremely easy to carry out for yarns’ basic performance [10]. In this study, the basic performances were tested for further research of their relationships to the knitted yarn strength utilization factor.
Specimen specifications of metallic yarns used in warp-knitting meshes are shown in
Specification of metallic yarns
No. | LF-1 yarn | LF-2 yarn | HF-1 yarn | HF-2 yarn |
---|---|---|---|---|
Material | Nickel-plated stainless steel wire | Gold-plated molybdenum wire | Gold-plated molybdenum wire | Molybdenum wire |
Diameter of monofilament (μm) | 30 | 27 | 17 | 16 |
Number of monofilaments | 3 | 3 | 4 | 4 |
Yarn linear density (tex) | 19.8 | 16.7 | 10.5 | 8.2 |
Twist Coefficient |
3.7 | 3.4 | 2.7 | 2.4 |
According to GB/T 3916-1997, tensile properties of metallic yarns were tested on a YG061-1500 yarn strength tensile instrument. The drawing gauge was 250mm, and the drawing speed was 20mm/min. Each sample was tested five times. The average value is shown in
Tensile properties of metallic yarns
No. | LF-1 yarn | LF-2 yarn | HF-1 yarn | HF-2 yarn |
---|---|---|---|---|
Breaking strength (cN) | 167.1 | 389.4 | 216.6 | 185.8 |
Elongation at break (%) | 23.8 | 1.8 | 2.0 | 1.9 |
A KES-FB2 bending tester was used for the bending stiffness test. Cardboard was cut into 11 mm pieces, with 60 yarns arranged in parallel (
Bending stiffness of metallic yarns
No. | LF-1 yarn | LF-2 yarn | HF-1 yarn | HF-2 yarn |
---|---|---|---|---|
Bending stiffness By (cN·cm2) | 0.0121 | 0.0152 | 0.0039 | 0.0037 |
Schematic diagram of specimen for bending test of yarns
LF-1 and LF-2 yarns were warp-knitted on an E16 warp-knitting machine with an open atlas tricot structure. In the process, two guide bars were adopted one in one out in a 4-line atlas lap, and closed loops were used in laying-in diversion. LF antennas were prepared with specific process parameters, shown in
Knitting process parameters for LF antennas
No. of mesh reflector | LF-1 mesh | LF-2 mesh | ||
---|---|---|---|---|
Materials | LF-1 yarn | LF-2 yarn | ||
Knitted structure | Open atlas tricot structure | Open atlas tricot structure | ||
Chain notation | Guide Bar 1 | Guide Bar 2 | Guide Bar 1 | Guide Bar 2 |
1-0/1-2/2-3/2-1// | 2-3/2-1/1-0/1-2// | 1-0/1-2/2-3/2-1// | 2-3/2-1/1-0/1-2// | |
Threading ways | 1*1* | 1*1* | 1*1* | 1*1* |
Let-of amount (mm/rack) | 2330 | 2370 | 2875 | 2870 |
Machine speed (mm/min) | 150-300 | 150-300 |
Knitting process parameters for HF antennas
No. of mesh reflector materials | HF-1 Mesh HF-1 yarn | HF-2 Mesh HF-2 yarn | ||
---|---|---|---|---|
Knitted structure | reverse locknit structure | reverse locknit structure | ||
Chain notation | Guide Bar 1 | Guide Bar 2 | Guide Bar 1 | Guide Bar 2 |
1-0/1-2// | 2-3/1-0// | 1-0/1-2// | 2-3/1-0// | |
Threading ways | Full | Full | Full | Full |
Let-of amount (mm/rack) | 2220 | 2370 | 2220 | 2690 |
Machine speed (mm/min) | 150-300 | 150-300 |
Warp-knitted mesh for LF antennas
Warp-knitted mesh for HF antennas
The test was conducted on a WDW-20 universal testing machine. The specimen length was 100 mm, and the width was 40 coils columns. The width of HF specimens was 20 columns of coils. Each specimen was tested 5 times along the longitudinal and transverse directions, respectively. The results are shown in
Tensile properties of warp-knitted meshes
Specimen specifications | Fracture strength (N) | Elongation at break (%) | |||
---|---|---|---|---|---|
LF-lmesh | Vertical | 100mmx30mm | Average value | 23.14 | 35.67 |
CV% | 14.68 | 18.87 | |||
Horizontal | 100mmx48mm | Average value | 17.79 | 96.13 | |
CV% | 8.24 | 5.9 | |||
LF-2 mesh | Vertical | 100mmx45mm | Average value | 29.30 | 52.23 |
CV% | 6.73 | 7.64 | |||
Horizontal | 100mmx40mm | Average value | 23.68 | 72.63 | |
CV% | 3.18 | 12.07 | |||
HF-1 mesh | Vertical | 100mmx25mm | Average value | 36.16 | 45.23 |
CV% | 7.49 | 2.56 | |||
Horizontal | 100mmxl5mm | Average value | 29.01 | 106.78 | |
CV% | 7.98 | 2.45 | |||
HF-2 mesh | Vertical | 100mmx25mm | Average value | 30.4 | 44.40 |
CV% | 10.5 | 2.35 | |||
Horizontal | 100mmx20mm | Average value | 25.93 | 126.10 | |
CV% | 2.38 | 2.63 |
The knittability of warp-knitted fabrics was able to be characterised by the damage degree of yarns after knitting. But warp-knitted fabrics could not be dislodged to obtain intact yarns against the knitting direction or with the knitting direction. Having been replaced, each knitted yarn’s strength utilization factor was calculated from single yarn’s tensile strength, which was obtained from the fabric’s tensile performance. The knitted yarn strength utilization factor could be used for knittability characterization. The higher the knitted yarn strength utilization factor, the better the knittability.
The number of yarns bearing loads during the tensile process was related to the stretching direction of the fabric. Mainly two yarns were loaded in longitudinal stretching, while only one in transverse stretching. Therefore, the fabric breakage strength was able to be calculated down to single yarn strength for a known number of stretched yarns [13].
In the longitudinal direction, 40 columns of LF-1and LF-2 specimens, which were actually 80 yarns, were stretched. 40 horizontal rows of LF-1 and LF-2, which were 40 yarns, were stretched along the transverse direction. While there were two overlapping loops in the HF-1 and HF-2 meshes, which amounted to 20 columns, with 80 yarns being stretched in the longitudinal direction, in the transverse direction, 20 horizontal rows including 40 yarns were stretched in HF-1 and HF-2 meshes.
From
Yarn strength after conversion based on metallic warp-knitted meshes
Mesh No. | Number of yarns in mesh | Strength of original yarn (N) | Strength of mesh (N) | Knitted yarn strength utilization factor (%) | |
---|---|---|---|---|---|
LF-1 | Vertical | 80 | 1.67 | 23.14 | 17.3 |
Horizontal | 40 | 17.79 | 26.6 | ||
LF-2 | Vertical | 80 | 3.89 | 29.30 | 9.4 |
Horizontal | 40 | 23.68 | 15.2 | ||
HF-1 | Vertical | 80 | 2.16 | 36.16 | 20.9 |
Horizontal | 40 | 29.01 | 33.6 | ||
HF-2 | Vertical | 80 | 1.85 | 30.4 | 20.5 |
Horizontal | 40 | 25.93 | 35.0 |
From
It can be seen from
It was shown that yarn elongation at break and yarn bending stiffness comprehensively affected the knittability of the yarns. To further investigate the quantitative relationship between yarn basic mechanical properties and yarn knittability, a multiple linear regression analysis was performed. The knitted yarn strength utilization factor was y1 and y2. The yarn elongation at break was x1, the yarn bending stiffness - x2, and the yarn breaking strength was x3. No reasonable fitting results were obtained. Based on the previous analysis, a reasonable fitting result should be obtained after removing the independent variable of the yarn breaking strength (x3). Results of the fitting of the knitted yarn strength utilization factor in the vertical and horizontal directions are shown in
Fitting results of multiple linear regression
Fitting equations | R2 | |
---|---|---|
Knitted yarn strength utilization factor in vertical direction y1 | yl =24.022+0.22x1-987.742x2 | 0.998 |
Knitted yarn strength utilization factor in horizontal direction y2 | y2=40.111+0.283x1-1672.848x2 | 0.998 |
As a result, a very strong linear relationship was found between y1(y2), x1, y1(y2) and x2. The coefficient (R2) of the prediction models was 0.998. The correlation between the elongation at break of yarn and the knitted yarn strength utilization factor was noticeable over 10% in both the vertical and horizontal directions. The correlation between bending stiffness and the knitted yarn strength utilization factor was over 5%. The yarn knittability could be quantitatively characterized by knitted yarn strength utilization factor. Therefore, the model shown in
In this study, the knittability of metallic yarn was successfully quantitatively characterized by the knitted yarn strength utilization factor. The effect of yarn mechanical properties on the knittability was further studied, including tensile strength and bending stiffness. Yarn breaking strength has no relationship with yarn knittability. The elongation at break had a native correlation to knittability, while stiffness showed a more significantly positive correlation. Ultimately, metallic yarns’ knittability should be improved by increasing yarn mechanical properties.