<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The influence of the cyclic loading on the functional properties of NiTi was studied. Cylindrical specimens with a diameter of 4 mm and a gage length of 12.5 mm were tested under uniaxial cyclic loading with control crosshead displacement at a temperature of 0°C. The dependences of the stress and strain range as well as dissipation energy on the number of loading cycles at different initial stress range were analysed. During the first 10 loading cycles, a rapid decrease in the strain range and energy dissipation was observed. Dissipation energy was invariant to the loading cycles’ number at N > 20 cycles and to the stress range that did not exceed the martensite finish stress level, was within the same scatter band and can be described by the single dependence. With the stress range growth at N &lt; 20 cycles from 509 to 740 MPa, the value of dissipation energy increases and that of relative dissipation energy decreases. Loss coefficient, which characterises material damping ability, significantly decreases during the first 10 loading cycles and remains practically unchanged up to the failure of the specimens. At the stabilisation area, the loss coefficient is almost non-sensitive towards the stress range.</p></abstract>

The influence of the cyclic loading on the functional properties of NiTi was studied. Cylindrical specimens with a diameter of 4 mm and a gage length of 12.5 mm were tested under uniaxial cyclic loading with control crosshead displacement at a temperature of 0°C. The dependences of the stress and strain range as well as dissipation energy on the number of loading cycles at different initial stress range were analysed. During the first 10 loading cycles, a rapid decrease in the strain range and energy dissipation was observed. Dissipation energy was invariant to the loading cycles’ number at N > 20 cycles and to the stress range that did not exceed the martensite finish stress level, was within the same scatter band and can be described by the single dependence. With the stress range growth at N < 20 cycles from 509 to 740 MPa, the value of dissipation energy increases and that of relative dissipation energy decreases. Loss coefficient, which characterises material damping ability, significantly decreases during the first 10 loading cycles and remains practically unchanged up to the failure of the specimens. At the stabilisation area, the loss coefficient is almost non-sensitive towards the stress range.

Degradation of Functional Properties of Pseudoelastic NiTi Alloy Under Cyclic Loading: An Experimental Study

Ternopil Ivan Puluj National Technical University

Acta Mechanica et Automatica

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The influence of the cyclic loading on the functional properties of NiTi was studied. Cylindrical specimens with a diameter of 4 mm and a gage length of 12.5...

Degradation of Functional Properties of Pseudoelastic NiTi Alloy Under Cyclic Loading: An Experimental Study

Publicado en línea: 25 jul 2019

Páginas: 95 - 100

Recibido: 14 mar 2019

Aceptado: 06 jun 2019

DOI: https://doi.org/10.2478/ama-2019-0013

Palabras clave
pseudoelastic alloy, functional properties, dissipation energy, strain range, stress range

© 2019 Volodymyr Iasnii et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Degradation of Functional Properties of Pseudoelastic NiTi Alloy Under Cyclic Loading: An Experimental Study

Publicado en línea: 25 jul 2019

Páginas: 95 - 100

Recibido: 14 mar 2019

Aceptado: 06 jun 2019

DOI: https://doi.org/10.2478/ama-2019-0013

Palabras clavepseudoelastic alloy, functional properties, dissipation energy, strain range, stress range

© 2019 Volodymyr Iasnii et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Palabras clave
pseudoelastic alloy, functional properties, dissipation energy, strain range, stress range