<abstract xmlns="http://www.w3.org/1999/xhtml">The article deals with the effect of porosity on the contact fatigue of sintered material type Astaloy CrL with 0.3 and 0.4% C. Sets of samples were used with densities beginning from the value of 7000 kg.m−3 to the value of almost 7859 kg.m−3 which represents almost zero porosity (compact material). It has been found out that the increase of compacting pressure applied simultaneously with temperature results in the reduction of porosity from the value of 9.10% to 0.0005% and increase in hardness from 145 to 193 HV10, depending on the carbon content. Logically there is also an increase in the fatigue life by the contact fatigue tests for the value of 50×106 cycles from the value of 900 MPa to 1150 MPa for samples with 0.3% of C and from 900 MPa to 1300 MPa for samples with 0.4% C. These investigations were also carried out in the past, but to achieve the reduction of porosity, different technonologies were used at each level such as double pressing, hot pressing, saturation, hot forging, etc. In this case, the single technology of “spark plasma sintering” making use of compacting at high temperatures is capable to continuously reduce porosity to zero.</abstract>

The article deals with the effect of porosity on the contact fatigue of sintered material type Astaloy CrL with 0.3 and 0.4% C. Sets of samples were used with densities beginning from the value of 7000 kg.m−3 to the value of almost 7859 kg.m−3 which represents almost zero porosity (compact material). It has been found out that the increase of compacting pressure applied simultaneously with temperature results in the reduction of porosity from the value of 9.10% to 0.0005% and increase in hardness from 145 to 193 HV10, depending on the carbon content. Logically there is also an increase in the fatigue life by the contact fatigue tests for the value of 50×106 cycles from the value of 900 MPa to 1150 MPa for samples with 0.3% of C and from 900 MPa to 1300 MPa for samples with 0.4% C. These investigations were also carried out in the past, but to achieve the reduction of porosity, different technonologies were used at each level such as double pressing, hot pressing, saturation, hot forging, etc. In this case, the single technology of “spark plasma sintering” making use of compacting at high temperatures is capable to continuously reduce porosity to zero.

Applying “Spark Plasma Sintering” Technology to Enhance the Resistance to Contact Fatigue of Sintered Steel Based on Astaloy CRL

Powder Metallurgy Progress

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The article deals with the effect of porosity on the contact fatigue of sintered material type Astaloy CrL with 0.3 and 0.4% C. Sets of samples were used with...

Applying “Spark Plasma Sintering” Technology to Enhance the Resistance to Contact Fatigue of Sintered Steel Based on Astaloy CRL

Publicado en línea: 21 dic 2017

Páginas: 21 - 28

DOI: https://doi.org/10.1515/pmp-2017-0003

Palabras clave
spark plasma sintering, Cr-sintered steel, contact fatigue

© 2017 D. Rodziňák et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Applying “Spark Plasma Sintering” Technology to Enhance the Resistance to Contact Fatigue of Sintered Steel Based on Astaloy CRL

Publicado en línea: 21 dic 2017

Páginas: 21 - 28

DOI: https://doi.org/10.1515/pmp-2017-0003

Palabras clavespark plasma sintering, Cr-sintered steel, contact fatigue

© 2017 D. Rodziňák et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Palabras clave
spark plasma sintering, Cr-sintered steel, contact fatigue