<abstract xmlns="http://www.w3.org/1999/xhtml">The magnetocaloric effect in the MnxFe2−xP1−yGey intermetallic compounds with the amount of Mn in the range of x = 1.05 to 1.17 and amount of Ge in the range of y = 0.19 to 0.22 has been studied. It was found that a higher Ge/P ratio causes an increase in Curie temperature, magnetocaloric effect at low field (up to 1 T), activation energy of structural transition and a decrease in thermal hysteresis, as well as transition enthalpy. Contrary to this observation, higher Mn/Fe ratio causes a decrease in Curie temperature, slight decrease of magnetocaloric effect at low magnetic field, and an increase in thermal hysteresis. Simultaneous increase of both ratios may be very advantageous, as the thermal hysteresis can be lowered and magnetocaloric effect can be enhanced without changing the Curie temperature. Some hints about optimization of the composition for applications at low magnetic fields (0.5 T to 2 T) have been presented.</abstract>

The magnetocaloric effect in the MnxFe2−xP1−yGey intermetallic compounds with the amount of Mn in the range of x = 1.05 to 1.17 and amount of Ge in the range of y = 0.19 to 0.22 has been studied. It was found that a higher Ge/P ratio causes an increase in Curie temperature, magnetocaloric effect at low field (up to 1 T), activation energy of structural transition and a decrease in thermal hysteresis, as well as transition enthalpy. Contrary to this observation, higher Mn/Fe ratio causes a decrease in Curie temperature, slight decrease of magnetocaloric effect at low magnetic field, and an increase in thermal hysteresis. Simultaneous increase of both ratios may be very advantageous, as the thermal hysteresis can be lowered and magnetocaloric effect can be enhanced without changing the Curie temperature. Some hints about optimization of the composition for applications at low magnetic fields (0.5 T to 2 T) have been presented.

Effect of changing P/Ge and Mn/Fe ratios on the magnetocaloric effect and structural transition in the (Mn,Fe)2 (P,Ge) intermetallic compounds

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Effect of changing P/Ge and Mn/Fe ratios on the magnetocaloric effect and structural transition in the (Mn,Fe) (P,Ge) intermetallic compounds

The magnetocaloric effect in the MnxFe2−xP1−yGey intermetallic compounds with the amount of Mn in the range of x = 1.05 to 1.17 and amount of Ge in the range...

Effect of changing P/Ge and Mn/Fe ratios on the magnetocaloric effect and structural transition in the (Mn,Fe)₂ (P,Ge) intermetallic compounds

Article Category: Research Article

Publicado en línea: 08 sept 2016

Páginas: 494 - 502

Recibido: 13 jul 2015

Aceptado: 24 may 2016

DOI: https://doi.org/10.1515/msp-2016-0068

Palabras clave
magnetocaloric effect, FeP type compounds, phase transition

© 2016 P. Wlodarczyk et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Effect of changing P/Ge and Mn/Fe ratios on the magnetocaloric effect and structural transition in the (Mn,Fe)2 (P,Ge) intermetallic compounds

Article Category: Research Article

Publicado en línea: 08 sept 2016

Páginas: 494 - 502

Recibido: 13 jul 2015

Aceptado: 24 may 2016

DOI: https://doi.org/10.1515/msp-2016-0068

Palabras clavemagnetocaloric effect, FeP type compounds, phase transition

© 2016 P. Wlodarczyk et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Effect of changing P/Ge and Mn/Fe ratios on the magnetocaloric effect and structural transition in the (Mn,Fe)₂ (P,Ge) intermetallic compounds

Palabras clave
magnetocaloric effect, FeP type compounds, phase transition