<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>This paper deals with the behavior of the ferritic-martensitic steel T91 samples covered with an AlTiN black coating, which is mainly used for high temperature applications (> 800 ° C) because of its resistance to oxidation. The coating was applied by use of a combination of High Power Impulse Magnetron Sputtering (HiPIMS) and Direct Current Magnetron Sputtering (DCMS). Samples were subjected to a tensile test in a static tank CALLISTO. The environment was liquid PbBi eutectic at a temperature of 550° C. Two types of samples, with a notch in the middle and without a notch, were tested. After exposure, the samples were subjected to morphological and chemical analyzes on SEM and EDX. Although the coating cracked over the entire length of the sample, high adhesion of the layer was demonstrated, the coating was delaminated locally only in the notch.</p></abstract>

This paper deals with the behavior of the ferritic-martensitic steel T91 samples covered with an AlTiN black coating, which is mainly used for high temperature applications (> 800 ° C) because of its resistance to oxidation. The coating was applied by use of a combination of High Power Impulse Magnetron Sputtering (HiPIMS) and Direct Current Magnetron Sputtering (DCMS). Samples were subjected to a tensile test in a static tank CALLISTO. The environment was liquid PbBi eutectic at a temperature of 550° C. Two types of samples, with a notch in the middle and without a notch, were tested. After exposure, the samples were subjected to morphological and chemical analyzes on SEM and EDX. Although the coating cracked over the entire length of the sample, high adhesion of the layer was demonstrated, the coating was delaminated locally only in the notch.

Analysis of the Coating for Heavy Liquid Metal Applications

KOM – Corrosion and Material Protection Journal

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

{"article-title":"Analysis of the Coating for Heavy Liquid Metal Applications"}

This paper deals with the behavior of the ferritic-martensitic steel T91 samples covered with an AlTiN black coating, which is mainly used for high temperature...

Analysis of the Coating for Heavy Liquid Metal Applications

Publicado en línea: 11 ene 2018

Páginas: 173 - 177

DOI: https://doi.org/10.1515/kom-2017-0022

© by J. Prehradná

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.