<abstract xmlns="http://www.w3.org/1999/xhtml"><p>In this paper research methods for detection of laminate panels damage were presented. The most common damage is: matrix cracking laminate interlayer damage to joints, connecting cracks, delamination and fiber breakage. The tested laminates will be used as assemblies and sub-assemblies of freight wagon. Other methods of modeling of machines by means of transducers are shown in Płaczek (2012, 2015) and Białas (2010). As part of the project authors were collaborated with specialists from other research centers and scientific research (Bocian and Kulisiewicz, 2013). As a part of future work the places where we will be able to replace the standard materials by parts made of laminate will be shown. Layered composites despite many advantages have also disadvantages. From last mentioned it is a relatively low resistance to transverse impact. When the laminate is used as a decorative element, its small damage is not a problem. The problems start when the composite satisfies more responsible tasks such as: is a part of the technical means for example of a railway wagon. Aspect of continuous monitoring of the technical state of the laminate is very important. Current technology provides numerous opportunities for non-destructive methods of technical inspections. In this paper method for testing of large areas, completely non-contact, based on the methods of thermography, was presented. It consists heating by using the composite tubes and examining it through a thermal imaging camera. Length of heating, and consequently the temperature to which the laminate is heated mostly were chosen experimentally. During the measurements, the camera measures the intensity of radiation, not temperature. Received thermogram is not always a precise representation of the actual temperature, because the camera does not reach only the radiation from tested object, but also reaches the radiation coming from the environment and reflected objects etc. As part of the research authors also we undertook other work related to Mechanical Engineering (Wróbel et al., 2008, 2010, 2012, 2013, 2015; Płaczek et al., 2014). Cooperation with other national and European centers has contributed to many publications of authors for example Tuma et al. (2013, 2014) and Jamroziak and Kosobudzki (2014).</p></abstract>

In this paper research methods for detection of laminate panels damage were presented. The most common damage is: matrix cracking laminate interlayer damage to joints, connecting cracks, delamination and fiber breakage. The tested laminates will be used as assemblies and sub-assemblies of freight wagon. Other methods of modeling of machines by means of transducers are shown in Płaczek (2012, 2015) and Białas (2010). As part of the project authors were collaborated with specialists from other research centers and scientific research (Bocian and Kulisiewicz, 2013). As a part of future work the places where we will be able to replace the standard materials by parts made of laminate will be shown. Layered composites despite many advantages have also disadvantages. From last mentioned it is a relatively low resistance to transverse impact. When the laminate is used as a decorative element, its small damage is not a problem. The problems start when the composite satisfies more responsible tasks such as: is a part of the technical means for example of a railway wagon. Aspect of continuous monitoring of the technical state of the laminate is very important. Current technology provides numerous opportunities for non-destructive methods of technical inspections. In this paper method for testing of large areas, completely non-contact, based on the methods of thermography, was presented. It consists heating by using the composite tubes and examining it through a thermal imaging camera. Length of heating, and consequently the temperature to which the laminate is heated mostly were chosen experimentally. During the measurements, the camera measures the intensity of radiation, not temperature. Received thermogram is not always a precise representation of the actual temperature, because the camera does not reach only the radiation from tested object, but also reaches the radiation coming from the environment and reflected objects etc. As part of the research authors also we undertook other work related to Mechanical Engineering (Wróbel et al., 2008, 2010, 2012, 2013, 2015; Płaczek et al., 2014). Cooperation with other national and European centers has contributed to many publications of authors for example Tuma et al. (2013, 2014) and Jamroziak and Kosobudzki (2014).

Testing of Composite Panels Used as Components of a Freight Wagon by Thermovision

Faculty of Mechanical Engineering, Silesian University of Technology, ul. Konarskiego 18A, 44-100 Gliwice, Poland

Acta Mechanica et Automatica

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

In this paper research methods for detection of laminate panels damage were presented. The most common damage is: matrix cracking laminate interlayer damage to...

Testing of Composite Panels Used as Components of a Freight Wagon by Thermovision

Publicado en línea: 07 mar 2016

Páginas: 17 - 21

Recibido: 22 sept 2014

Aceptado: 22 dic 2015

DOI: https://doi.org/10.1515/ama-2016-0003

Palabras clave
Thermovision, Components, Testing, Panels, Imaging Method

© 2016 Bialystok University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Testing of Composite Panels Used as Components of a Freight Wagon by Thermovision

Publicado en línea: 07 mar 2016

Páginas: 17 - 21

Recibido: 22 sept 2014

Aceptado: 22 dic 2015

DOI: https://doi.org/10.1515/ama-2016-0003

Palabras claveThermovision, Components, Testing, Panels, Imaging Method

© 2016 Bialystok University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
Thermovision, Components, Testing, Panels, Imaging Method