The Effect of Long Term Service at Elevated Temperatures on Microstructure Degradation of Austenitic Reformer Tubes

1. Łabanowski J., Assessment of catalytic tubes degradation of reformer units in service. Gdansk University of Technology, Gdansk 2003 (in Polish).Search in Google Scholar

2. Łabanowski J., Jurkowski M., Landowski M., Effect of Long Term Service at Elevated Temperatures on Mechanical Properties of Manaurite XM Reformer Tubes. Advances in Materials Science, 16(4) (2016) 38÷44.10.1515/adms-2016-0021Search in Google Scholar

3. Le May I., da Silveira T. L., Vianna C. H.: Criteria for the evaluation of damage and remaining life in reformer furnace tube. International Journal of Pressure Vessels and Piping 66 (1996) 233÷241.10.1016/0308-0161(95)00098-4Search in Google Scholar

4. Ray A. K., Sinha S. K., Tiwari Y. N., Swaminathan J., Das G., Chaudhuri S., Singh R.: Analysis of failed reformer tubes. Engineering Failure Analysis, 10 (2003) 351÷362.10.1016/S1350-6307(02)00029-8Search in Google Scholar

5. Manoir Industries: http://www.manoir-industries.com/site/docs_wsw/fichiers_communs/docs/MI_Manaurite_XM.pdfSearch in Google Scholar

6. Wen S., Xuezhi Q., Jianting G., Langhong L., Lanzhang Z.: Microstructure stability and mechanical properties of a new low cost hot-corrosion resistant Ni-Fe-Cr based superalloy during long-term thermal exposure. Materials and Design, 69 (2015) 70÷80.Search in Google Scholar

7. Wahab A. A., Hutchinson C. R., Kral M. V., Three-dimensional characterization of creep void formation in hydrogen reformer tubes. Scripta Materialia, 55 (2006) 69÷73.Search in Google Scholar

8. Alvino An., Lega D., Giacobbe F., Mazzocchi V., Rinaldi A.: Damage characterization in two reformer heater tubes after nearly 10 years of service at different operative and maintenance conditions. Engineering Failure Analysis, 17 (2010) 1526÷1541.Search in Google Scholar

9. Chen Q. Z., Thomas C. W., Knowles D. M., Characterisation of 20Cr32Ni1Nb alloys in as-cast and Ex-Service conditions by SEM, TEM and EDX. Materials Science and Engineering A, 374 (2004) 398÷408.Search in Google Scholar

10. Sustaita-Torres I. A., Haro-Rodriguez S., Guerrero-Mata M. P., de la Garza M., Valdes E., Deschaux-Beaume F., Colas R.: Aging of a cast 35Cr-45Ni heat resistant alloy. Materials Chemistry and Physics, 133 (2012) 1018÷1023.Search in Google Scholar

11. Łabanowski J.: Evaluation of reformer tubes degradation after long term operation. Journal of Achievements in Materials and Manufacturing Engineering, 43 (1) (2010) 244÷251.Search in Google Scholar

12. Lee J. H., Yang W. J., Yoo W. D., Cho K. S., Microstructural and mechanical property changes in HK40 reformer tubes after long term use. Engineering Failure Analysis, 16 (2009) 1883÷1888.Search in Google Scholar

13. Kondrat’ev S.Y., Kraposhin V.S., Anastasiadi G.P., Talis A.L., Experimental observation and crystallographic description of M7C3 carbide transformation in Fe-Cr-Ni-C HP type alloy. Acta Materialia, 100 (2015) 275÷281.Search in Google Scholar

14. Laigo J., Christien F., Le Gall R., Tancret F., Furtado J., SE, EDS, EPMA-WDA and EBSD characterization of carbides in HP type heat resistant alloys. Materials Characterization, 59 (2008) 1580÷1586.Search in Google Scholar