<abstract xmlns="http://www.w3.org/1999/xhtml">The paper presents properties of surface layers. Surface layers were obtained by using low temperature glow–discharge nitriding process and laser remelting carried out on austenitic stainless steel type X10CrNi18-8. Investigations were done by using an Ultra Nanoindentation Tester (UNHT) in the Warsaw Institute of Fundamental Technological Research. The influence of the above mentioned treatments on obtained surface layers is shown. The values of the Vickers hardness (HV), the irreversible indentation work (Wir), the reversible work (We) and the maximum depth (hmax) during indentation were determined using the method proposed by Oliver and Pharr [1]. On the basis of mechanical properties, the elasticity (Ie) and ductility (Iir) indexes were calculated. Moreover, microstructure cross-section of the austenitic stainless steel after nitriding process and laser remelting was observed using a scanning electron microscope. Cavitation test was performed at a vibratory rig with stationary specimen. On the basis of erosion curves the cavitation resistance was evaluated.</abstract>

The paper presents properties of surface layers. Surface layers were obtained by using low temperature glow–discharge nitriding process and laser remelting carried out on austenitic stainless steel type X10CrNi18-8. Investigations were done by using an Ultra Nanoindentation Tester (UNHT) in the Warsaw Institute of Fundamental Technological Research. The influence of the above mentioned treatments on obtained surface layers is shown. The values of the Vickers hardness (HV), the irreversible indentation work (Wir), the reversible work (We) and the maximum depth (hmax) during indentation were determined using the method proposed by Oliver and Pharr [1]. On the basis of mechanical properties, the elasticity (Ie) and ductility (Iir) indexes were calculated. Moreover, microstructure cross-section of the austenitic stainless steel after nitriding process and laser remelting was observed using a scanning electron microscope. Cavitation test was performed at a vibratory rig with stationary specimen. On the basis of erosion curves the cavitation resistance was evaluated.

Influence of Nitriding and Laser Remelting on Properties of Austenitic Stainless Steel Type X10CrNi18-8 and Cavitation Erosion Resistance

Gdańsk University of Technology, Faculty of Mechanical Engineering, Department of Materials Technology and Welding, 11/12 Narutowicza, 80-233 Gdańsk, Poland

Institute of Fundamental Technological Research of the Polish Academy of Sciences, Department of Mechanics of Materials, Pawińskiego 5B, 02-106 Warsaw, Poland

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The paper presents properties of surface layers. Surface layers were obtained by using low temperature glow–discharge nitriding process and laser remelting...

Influence of Nitriding and Laser Remelting on Properties of Austenitic Stainless Steel Type X10CrNi18-8 and Cavitation Erosion Resistance

Publicado en línea: 02 ago 2016

Páginas: 21 - 31

DOI: https://doi.org/10.1515/adms-2016-0006

Palabras clave
glow-discharge nitriding process, laser remelting, austenitic stainless steel, diffusion layer, nitrided case, expanded austenite

© 2016 A. Sitko et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Influence of Nitriding and Laser Remelting on Properties of Austenitic Stainless Steel Type X10CrNi18-8 and Cavitation Erosion Resistance

Publicado en línea: 02 ago 2016

Páginas: 21 - 31

DOI: https://doi.org/10.1515/adms-2016-0006

Palabras claveglow-discharge nitriding process, laser remelting, austenitic stainless steel, diffusion layer, nitrided case, expanded austenite

© 2016 A. Sitko et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
glow-discharge nitriding process, laser remelting, austenitic stainless steel, diffusion layer, nitrided case, expanded austenite