<abstract xmlns="http://www.w3.org/1999/xhtml">The paper presents the results of a study on the corrosion behaviour of copper (EN CW004A) in five possible phase change materials (PCMs): magnesium nitrate hexahydrate pure and with an addition of Mg(OH)2 (0.5 wt. %) or Sr(OH)2 (0.5 wt. %) at 90 °C, calcium nitrate tetrahydrate at 50 °C and a mixture of magnesium nitrate hexahydrate and calcium nitrate tetrahydrate (1:1 mass ratio) at 72 °C. The corrosion rate of copper samples is low except for the use of Mg(NO3)2 · 6H2O with/without an addition of Mg(OH)2. The lowest corrosion rate was observed for the mixture Mg(NO3)2 · 6H2O—Ca(NO3)2 · 4H2O (1:1), and it was ca six times lower than that of pure magnesium nitrate hexahydrate.</abstract>

The paper presents the results of a study on the corrosion behaviour of copper (EN CW004A) in five possible phase change materials (PCMs): magnesium nitrate hexahydrate pure and with an addition of Mg(OH)2 (0.5 wt. %) or Sr(OH)2 (0.5 wt. %) at 90 °C, calcium nitrate tetrahydrate at 50 °C and a mixture of magnesium nitrate hexahydrate and calcium nitrate tetrahydrate (1:1 mass ratio) at 72 °C. The corrosion rate of copper samples is low except for the use of Mg(NO3)2 · 6H2O with/without an addition of Mg(OH)2. The lowest corrosion rate was observed for the mixture Mg(NO3)2 · 6H2O—Ca(NO3)2 · 4H2O (1:1), and it was ca six times lower than that of pure magnesium nitrate hexahydrate.

Corrosive effects of nitrate-containing phase change materials used with copper

Slovak University of Technology in Bratislava, Institute of Inorganic Chemistry, Technology and Materials, Radlinského 9, SK – 812 37 Bratislava,

Acta Chimica Slovaca

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Corrosive effects of nitrate-containing phase change materials used with copper"}

The paper presents the results of a study on the corrosion behaviour of copper (EN CW004A) in five possible phase change materials (PCMs): magnesium nitrate...

Corrosive effects of nitrate-containing phase change materials used with copper

Publicado en línea: 08 dic 2016

Páginas: 75 - 83

DOI: https://doi.org/10.1515/acs-2016-0013

Palabras clave
phase change materials, latent heat storage, magnesium nitrate, calcium nitrate, copper, corrosion rate

© 2016 Faculty of Chemical and Food Technology, Slovak University of Technology in Bratislava

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Corrosive effects of nitrate-containing phase change materials used with copper

Publicado en línea: 08 dic 2016

Páginas: 75 - 83

DOI: https://doi.org/10.1515/acs-2016-0013

Palabras clavephase change materials, latent heat storage, magnesium nitrate, calcium nitrate, copper, corrosion rate

© 2016 Faculty of Chemical and Food Technology, Slovak University of Technology in Bratislava

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
phase change materials, latent heat storage, magnesium nitrate, calcium nitrate, copper, corrosion rate