<abstract xmlns="http://www.w3.org/1999/xhtml"> Background: Scaffolds for bone tissue engineering must meet functional requirements, porosity, biocompatibility, and biodegradability. Different polymeric scaffolds have been designed to satisfy these properties. Composite materials could improve mechanical properties compared with polymers, and structural integrity and flexibility compared with brittle ceramics.Objective: Fabricate poly (lactic-co-glycolic acid) (PLGA) /hydroxyapatite (HA) porous scaffolds by freezeextraction method, and evaluate the possibility for optimizing their biocompatibility by changing their HA content.Methods: Porous PLGA/HA composites structure were prepared by freezing a polymer solution, and then the solvent was extracted by a non-solvent and subsequently air-dried. The scaffolds were coated with triblock copolymer and sterilized by ultraviolet light. Human mesenchymal stem cells were cultured on the prepared scaffolds and were studied after three days by 4, 6-diamidino-2-phenylindole (DAPI) fluorescence microscopy.Results: Microstructural studies with SEM showed the formation of about 50 micrometer size porous structure and interconnected porosity so that cells were adhered well into the structure of the coated samples. DAPI fluorescence microscopy showed more cell adhesion to the coated scaffolds and cell diffusion into the pores are visible. Direct assay of cell proliferation performed with MTT test showed cell growing on the scaffold similar to or more than on control samples.Conclusion: The triblock-coated PLGA/HA porous scaffolds may provide cell adhesion and proliferation, demonstrating their potential application in bone engineering.</abstract>

Background: Scaffolds for bone tissue engineering must meet functional requirements, porosity, biocompatibility, and biodegradability. Different polymeric scaffolds have been designed to satisfy these properties. Composite materials could improve mechanical properties compared with polymers, and structural integrity and flexibility compared with brittle ceramics.Objective: Fabricate poly (lactic-co-glycolic acid) (PLGA) /hydroxyapatite (HA) porous scaffolds by freezeextraction method, and evaluate the possibility for optimizing their biocompatibility by changing their HA content.Methods: Porous PLGA/HA composites structure were prepared by freezing a polymer solution, and then the solvent was extracted by a non-solvent and subsequently air-dried. The scaffolds were coated with triblock copolymer and sterilized by ultraviolet light. Human mesenchymal stem cells were cultured on the prepared scaffolds and were studied after three days by 4, 6-diamidino-2-phenylindole (DAPI) fluorescence microscopy.Results: Microstructural studies with SEM showed the formation of about 50 micrometer size porous structure and interconnected porosity so that cells were adhered well into the structure of the coated samples. DAPI fluorescence microscopy showed more cell adhesion to the coated scaffolds and cell diffusion into the pores are visible. Direct assay of cell proliferation performed with MTT test showed cell growing on the scaffold similar to or more than on control samples.Conclusion: The triblock-coated PLGA/HA porous scaffolds may provide cell adhesion and proliferation, demonstrating their potential application in bone engineering.

Brief communication (Original). Preparation of a novel porous scaffold from poly(lactic-co-glycolic acid)/hydroxyapatite

New Technologies Research Center, Amirkabir University of Technology, Tehran 15916-33311;

Biomaterials Research Center, University of Tehran, Tehran 13145-1384;

Stem Cells Technology Research Center, Tehran 15856-36473,

Asian Biomedicine

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Background: Scaffolds for bone tissue engineering must meet functional requirements, porosity, biocompatibility, and biodegradability. Different polymeric...

Brief communication (Original). Preparation of a novel porous scaffold from poly(lactic-co-glycolic acid)/hydroxyapatite

Online veröffentlicht: 04. Feb. 2017

Seitenbereich: 513 - 518

DOI: https://doi.org/10.5372/1905-7415.0504.067

Schlüsselwörter
Cell adhesion, composite, freeze-extraction, human mesenchymal stem cells (hMSC), porous scaffold, tissue engineering

© 2017

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Brief communication (Original). Preparation of a novel porous scaffold from poly(lactic-co-glycolic acid)/hydroxyapatite

Online veröffentlicht: 04. Feb. 2017

Seitenbereich: 513 - 518

DOI: https://doi.org/10.5372/1905-7415.0504.067

SchlüsselwörterCell adhesion, composite, freeze-extraction, human mesenchymal stem cells (hMSC), porous scaffold, tissue engineering

© 2017

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
Cell adhesion, composite, freeze-extraction, human mesenchymal stem cells (hMSC), porous scaffold, tissue engineering