<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Martensitic β→α′(α″) and β→ω transformation in a series of Ti-base alloys with transition metals of groups IV-VIII have been investigated using the techniques of X-ray diffraction, optical and transmission electron microscopy. Phase and structural information is given on the non-equilibrium and metastable modifications occurring in these alloys during quenching from high-temperature β-field and aging. The conditions of the orthorhombic ″-phase, ω-phase and metastable β-phase formation in binary titanium-base alloys with <italic>d</italic>-metals of V-VIII groups were investigated. It was established that the position of the alloying metal in the Periodic Table defines the presence or absence of the ″-phase in the alloy after quenching and the minimum concentration of the alloying metal necessary for formation of the ″-phase, ω-phase and metastable β-phase.</p></abstract>

Martensitic β→α′(α″) and β→ω transformation in a series of Ti-base alloys with transition metals of groups IV-VIII have been investigated using the techniques of X-ray diffraction, optical and transmission electron microscopy. Phase and structural information is given on the non-equilibrium and metastable modifications occurring in these alloys during quenching from high-temperature β-field and aging. The conditions of the orthorhombic ″-phase, ω-phase and metastable β-phase formation in binary titanium-base alloys with d-metals of V-VIII groups were investigated. It was established that the position of the alloying metal in the Periodic Table defines the presence or absence of the ″-phase in the alloy after quenching and the minimum concentration of the alloying metal necessary for formation of the ″-phase, ω-phase and metastable β-phase.

The Regularities of Phase and Structural Transformation in Binary Titanium Alloys with Metals of IV—VIII Groups of the Periodic Table

Institute of Metal Physics, Ural Branch of Russian Academy of Sciences, Ekaterinburg, Russia

Advances in Materials Science

Martensitic β→α′(α″) and β→ω transformation in a series of Ti-base alloys with transition metals of groups IV-VIII have been investigated using the techniques...

The Regularities of Phase and Structural Transformation in Binary Titanium Alloys with Metals of IV—VIII Groups of the Periodic Table

Online veröffentlicht: 23. Sept. 2008

Seitenbereich: 37 - 42

DOI: https://doi.org/10.2478/v10077-008-0004-7

Schlüsselwörter
titanium alloys, phase transformation, ″-phase, ω-phase, metastable β-phase

This content is open access.

The Regularities of Phase and Structural Transformation in Binary Titanium Alloys with Metals of IV—VIII Groups of the Periodic Table

Online veröffentlicht: 23. Sept. 2008

Seitenbereich: 37 - 42

DOI: https://doi.org/10.2478/v10077-008-0004-7

Schlüsselwörtertitanium alloys, phase transformation, ″-phase, ω-phase, metastable β-phase