<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml">This contribution deals with the preparation and characterization of bismuth-doped yttrium iron garnets with composition BiY2Fe5O12 (Bi:YIG). The samples have been prepared by sintering of metal oxides homogenized in acetone for 10 minutes. The estimated average crystallite size of the single phase Bi:YIG synthesized at temperature 950 °C for 15 hours is ~ 65 nm. The real content of Bi3+ cations in samples was quantitatively evaluated by application of real-coded genetic algorithm to the powder X-ray diffraction patterns.</abstract>

This contribution deals with the preparation and characterization of bismuth-doped yttrium iron garnets with composition BiY2Fe5O12 (Bi:YIG). The samples have been prepared by sintering of metal oxides homogenized in acetone for 10 minutes. The estimated average crystallite size of the single phase Bi:YIG synthesized at temperature 950 °C for 15 hours is ~ 65 nm. The real content of Bi3+ cations in samples was quantitatively evaluated by application of real-coded genetic algorithm to the powder X-ray diffraction patterns.

Thermal Synthesis of Bismuth-Doped Yttrium Iron Garnet for Magneto-Optical Imaging

Institute of Measurement Science, Slovak Academy of Sciences, Dúbravská cesta 9, SK-841 04 Bratislava, Slovakia

Measurement Science Review

This contribution deals with the preparation and characterization of bismuth-doped yttrium iron garnets with composition BiY2Fe5O12 (Bi:YIG). The samples have...

Thermal Synthesis of Bismuth-Doped Yttrium Iron Garnet for Magneto-Optical Imaging

Online veröffentlicht: 24. Okt. 2008

Seitenbereich: 126 - 128

DOI: https://doi.org/10.2478/v10048-008-0030-y

Schlüsselwörter
bismuth-doped yttrium iron garnet, synthesis, TGA/DTA, XRD, real-coded genetic algorithm

This content is open access.

Thermal Synthesis of Bismuth-Doped Yttrium Iron Garnet for Magneto-Optical Imaging

Online veröffentlicht: 24. Okt. 2008

Seitenbereich: 126 - 128

DOI: https://doi.org/10.2478/v10048-008-0030-y

Schlüsselwörterbismuth-doped yttrium iron garnet, synthesis, TGA/DTA, XRD, real-coded genetic algorithm

This content is open access.

Schlüsselwörter
bismuth-doped yttrium iron garnet, synthesis, TGA/DTA, XRD, real-coded genetic algorithm