<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml">The influence of the process temperature from 85°C to 95°C, the content of phosphates and sulphates in the wet process phosphoric acid (about 22-36 wt% P2O5 and about 2-9 wt% SO42-) and the addition of αCaSO4·0.5H2O crystallization nuclei (from 10% to 50% in relation to CaSO4·2H2O) on the transformation of calcium sulphate dihydrate to hemihydrate has been determined. The wet process phosphoric acid and phosphogypsum from the industrial plant was utilized. They were produced by reacting sulphuric acid with phosphate rock (Tunisia) in the DH-process. The X-ray diffraction analysis was used to determine the phase composition and fractions of various forms of calcium sulphates in the samples and the degree of conversion of CaSO4·2H2O to αCaSO4·0.5H2O and CaSO4. It was found that the transformation of CaSO4·2H2O to αCaSO4·0.5H2O should be carried out in the presence of αCaSO4·0.5H2O crystallization nuclei as an additive (in the amount of 20% in relation to CaSO4·2H2O), at temperatures 90±2°C, in the wet process phosphoric acid containing the sulphates and phosphates in the range of 4±1 wt% and 27±1 wt%, respectively.</abstract>

The influence of the process temperature from 85°C to 95°C, the content of phosphates and sulphates in the wet process phosphoric acid (about 22-36 wt% P2O5 and about 2-9 wt% SO42-) and the addition of αCaSO4·0.5H2O crystallization nuclei (from 10% to 50% in relation to CaSO4·2H2O) on the transformation of calcium sulphate dihydrate to hemihydrate has been determined. The wet process phosphoric acid and phosphogypsum from the industrial plant was utilized. They were produced by reacting sulphuric acid with phosphate rock (Tunisia) in the DH-process. The X-ray diffraction analysis was used to determine the phase composition and fractions of various forms of calcium sulphates in the samples and the degree of conversion of CaSO4·2H2O to αCaSO4·0.5H2O and CaSO4. It was found that the transformation of CaSO4·2H2O to αCaSO4·0.5H2O should be carried out in the presence of αCaSO4·0.5H2O crystallization nuclei as an additive (in the amount of 20% in relation to CaSO4·2H2O), at temperatures 90±2°C, in the wet process phosphoric acid containing the sulphates and phosphates in the range of 4±1 wt% and 27±1 wt%, respectively.

Studies on the transformation of calcium sulphate dihydrate to hemihydrate in the wet process phosphoric acid production

Institute of Chemical and Environment Engineering, West Pomeranian University of Technology, Szczecin, ul. Pułaskiego 10, 70-322 Szczecin, Poland

Polish Journal of Chemical Technology

The influence of the process temperature from 85°C to 95°C, the content of phosphates and sulphates in the wet process phosphoric acid (about 22-36 wt% P2O5...

Studies on the transformation of calcium sulphate dihydrate to hemihydrate in the wet process phosphoric acid production

Online veröffentlicht: 02. Juli 2012

Seitenbereich: 80 - 87

DOI: https://doi.org/10.2478/v10026-012-0075-4

Schlüsselwörter
wet process phosphoric acid, phosphogypsum, transformation, calcium hemihydrate

This content is open access.

Studies on the transformation of calcium sulphate dihydrate to hemihydrate in the wet process phosphoric acid production

Online veröffentlicht: 02. Juli 2012

Seitenbereich: 80 - 87

DOI: https://doi.org/10.2478/v10026-012-0075-4

Schlüsselwörterwet process phosphoric acid, phosphogypsum, transformation, calcium hemihydrate

This content is open access.

Schlüsselwörter
wet process phosphoric acid, phosphogypsum, transformation, calcium hemihydrate