<p>The process parameters of the Laser Metal Deposition technology in the production of simple components made of NiCuBSi type metal powder were verified in this paper. A laser head with a coaxial powder supply and argon gas was used in the production. The powder was welded to a S235J2G3 steel plate. The used parameters (heat input 0.25 kJ.mm<sup>−1</sup>) enabled the production of samples with a minimum porosity (1.2 %) and without the defects (cold joints, pores) between the weld layers.</p>
</abstract>

The process parameters of the Laser Metal Deposition technology in the production of simple components made of NiCuBSi type metal powder were verified in this paper. A laser head with a coaxial powder supply and argon gas was used in the production. The powder was welded to a S235J2G3 steel plate. The used parameters (heat input 0.25 kJ.mm−1) enabled the production of samples with a minimum porosity (1.2 %) and without the defects (cold joints, pores) between the weld layers.

Use of Laser Metal Deposition Technology in Additive Manufacturing of Ni Powder Materials

Slovak University of Technology in Bratislava, Faculty of Mechanical Engineering

Strojnícky časopis - Journal of Mechanical Engineering

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The process parameters of the Laser Metal Deposition technology in the production of simple components made of NiCuBSi type metal powder were verified in this...

Use of Laser Metal Deposition Technology in Additive Manufacturing of Ni Powder Materials

Online veröffentlicht: 07. Nov. 2022

Seitenbereich: 161 - 172

DOI: https://doi.org/10.2478/scjme-2022-0026

Schlüsselwörter
additive manufacturing, Laser Metal Deposition, self-fluxing NiCuBSi metal powder

© 2022 Sejč Pavol et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Use of Laser Metal Deposition Technology in Additive Manufacturing of Ni Powder Materials

Online veröffentlicht: 07. Nov. 2022

Seitenbereich: 161 - 172

DOI: https://doi.org/10.2478/scjme-2022-0026

Schlüsselwörteradditive manufacturing, Laser Metal Deposition, self-fluxing NiCuBSi metal powder

© 2022 Sejč Pavol et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
additive manufacturing, Laser Metal Deposition, self-fluxing NiCuBSi metal powder