<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>An effective process for the synthesis of nano spinel zinc ferrite/expanded graphite composites was developed in order to get an electromagnetic interference shielding material. Firstly, expandable graphite was prepared using sulfuric and nitric acid solutions. Then, the precursor of the composites was produced by chemical co-precipitation method, followed by heating treatment. The obtained composites were characterized by X-ray diffraction and scanning electron microscopy. The dielectric and magnetic properties were determined using vector network analyzer and vibrating sample magnetometry. The results showed that ferrite nanoparticles with the sizes of about 50–150 nm were uniformly dispersed on the surface and interspace of EG. The magnetic properties of the composites changed by adjusting the ferrite/EG ratio and the composites had high dielectric constant in the range of 2–18 GHz. These properties of the prepared composites suggest that they can be used as a promising electromagnetic interference shielding material.</p></abstract>

An effective process for the synthesis of nano spinel zinc ferrite/expanded graphite composites was developed in order to get an electromagnetic interference shielding material. Firstly, expandable graphite was prepared using sulfuric and nitric acid solutions. Then, the precursor of the composites was produced by chemical co-precipitation method, followed by heating treatment. The obtained composites were characterized by X-ray diffraction and scanning electron microscopy. The dielectric and magnetic properties were determined using vector network analyzer and vibrating sample magnetometry. The results showed that ferrite nanoparticles with the sizes of about 50–150 nm were uniformly dispersed on the surface and interspace of EG. The magnetic properties of the composites changed by adjusting the ferrite/EG ratio and the composites had high dielectric constant in the range of 2–18 GHz. These properties of the prepared composites suggest that they can be used as a promising electromagnetic interference shielding material.

Preparation and electromagnetic properties of zinc ferrite/expanded graphite composites

School of Physics and Optoelectronic Engineering, Nanjing University of Information Science & Technology, Nanjing, 210044, China

Shanghai Research Institute of Chemical Industry, Shanghai, 200062, China

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

An effective process for the synthesis of nano spinel zinc ferrite/expanded graphite composites was developed in order to get an electromagnetic interference...

Preparation and electromagnetic properties of zinc ferrite/expanded graphite composites

Online veröffentlicht: 17. Okt. 2014

Seitenbereich: 470 - 474

DOI: https://doi.org/10.2478/s13536-014-0209-x

Schlüsselwörter
ferrite, graphite, composites, nanocomposites, magnetic properties

© 2014 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Preparation and electromagnetic properties of zinc ferrite/expanded graphite composites

Online veröffentlicht: 17. Okt. 2014

Seitenbereich: 470 - 474

DOI: https://doi.org/10.2478/s13536-014-0209-x

Schlüsselwörterferrite, graphite, composites, nanocomposites, magnetic properties

© 2014 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
ferrite, graphite, composites, nanocomposites, magnetic properties