<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Nanocrystalline tricalcium phosphate powder was synthesized via the solution-precipitation method followed by heat treatment in order to achieve phase evolution, which was then studied by XRD and TEM techniques. The crystallites sizes were estimated by the Scherrer method and results were confirmed by TEM micrographs. The experimental observations showed that nanocrystalline tricalcium phosphate can be successfully prepared from raw materials by the precipitation technique. This technique is a competitive method for nanocrystalline tricalcium phosphate synthesis compared to other techniques. Moreover, a simple kinetic growth investigation was performed on the nanocrystalline growth process during heat treatment. Results have shown growth rate to increase exponentially with temperature and the growth rate constants to increase with time. The average activation energies of tricalcium phosphate grain growth obtained by this method were 84.78 and 134.38 KJ/mol.</p></abstract>

Nanocrystalline tricalcium phosphate powder was synthesized via the solution-precipitation method followed by heat treatment in order to achieve phase evolution, which was then studied by XRD and TEM techniques. The crystallites sizes were estimated by the Scherrer method and results were confirmed by TEM micrographs. The experimental observations showed that nanocrystalline tricalcium phosphate can be successfully prepared from raw materials by the precipitation technique. This technique is a competitive method for nanocrystalline tricalcium phosphate synthesis compared to other techniques. Moreover, a simple kinetic growth investigation was performed on the nanocrystalline growth process during heat treatment. Results have shown growth rate to increase exponentially with temperature and the growth rate constants to increase with time. The average activation energies of tricalcium phosphate grain growth obtained by this method were 84.78 and 134.38 KJ/mol.

Effect of heat-treatment on grain growth of nanocrystalline tricalcium phosphate powder synthesized via the precipitation method

Ceramics Department, Materials and Energy Research Center, P.O. Box 31787-316, Tehran, Iran

Ceramics Department, Shahrood branch, Islamic Azad University, Shahrood, Iran

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Nanocrystalline tricalcium phosphate powder was synthesized via the solution-precipitation method followed by heat treatment in order to achieve phase...

Effect of heat-treatment on grain growth of nanocrystalline tricalcium phosphate powder synthesized via the precipitation method

Online veröffentlicht: 29. Feb. 2012

Seitenbereich: 203 - 208

DOI: https://doi.org/10.2478/s13536-011-0032-6

Schlüsselwörter
tricalcium phosphate, nanostructures, crystal growth, electron microscopy, X-ray diffraction

© 2011 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Effect of heat-treatment on grain growth of nanocrystalline tricalcium phosphate powder synthesized via the precipitation method

Online veröffentlicht: 29. Feb. 2012

Seitenbereich: 203 - 208

DOI: https://doi.org/10.2478/s13536-011-0032-6

Schlüsselwörtertricalcium phosphate, nanostructures, crystal growth, electron microscopy, X-ray diffraction

© 2011 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
tricalcium phosphate, nanostructures, crystal growth, electron microscopy, X-ray diffraction