<p>Thermal insulation materials used in civil engineering have been developing throughout time. One of the latest thermal insulation used in construction sites with gained popularity is EPS aggregate and mineral binder-based composite. Waste recycling potential, low cost, and ease of installation have brought popularity to the material. This research investigates such material which is formulated by EPS aggregates and pure Portland cement binder thus making EPS aggregate concrete (EAC). Many contractors use such untested and uncertified EAC material due to the low cost of the raw materials. In this research, EAC was taken directly from the construction site. Material physical and mechanical properties are evaluated and compared to commercial counterparts. The drying of the material was investigated, following the practice in the construction sites where upper covering layers are built according to the time schedule ignoring material drying process. Results were compared with commercial EAC. Results indicate that rapid construction schedule with layer-to-layer covering of wet EAC results in dramatically slow drying of such composites, which is one of the main problems for safe use in civil engineering. EAC density from 113 to 169 kg/m<sup>3</sup> was measured with an average compressive strength of 49 kPa. The thermal conductivity of the tested EAC was from 0.050 to 0.055 W/(mK).</p>
</abstract>

Thermal insulation materials used in civil engineering have been developing throughout time. One of the latest thermal insulation used in construction sites with gained popularity is EPS aggregate and mineral binder-based composite. Waste recycling potential, low cost, and ease of installation have brought popularity to the material. This research investigates such material which is formulated by EPS aggregates and pure Portland cement binder thus making EPS aggregate concrete (EAC). Many contractors use such untested and uncertified EAC material due to the low cost of the raw materials. In this research, EAC was taken directly from the construction site. Material physical and mechanical properties are evaluated and compared to commercial counterparts. The drying of the material was investigated, following the practice in the construction sites where upper covering layers are built according to the time schedule ignoring material drying process. Results were compared with commercial EAC. Results indicate that rapid construction schedule with layer-to-layer covering of wet EAC results in dramatically slow drying of such composites, which is one of the main problems for safe use in civil engineering. EAC density from 113 to 169 kg/m3 was measured with an average compressive strength of 49 kPa. The thermal conductivity of the tested EAC was from 0.050 to 0.055 W/(mK).

Case Study of EPS Aggregate Insulation Material Used in Construction Sites

Department of Building Materials and Products

Environmental and Climate Technologies

This work is licensed under the Creative Commons Attribution 4.0 International License.

{"article-title":"Case Study of EPS Aggregate Insulation Material Used in Construction Sites"}

Thermal insulation materials used in civil engineering have been developing throughout time. One of the latest thermal insulation used in construction sites...

Case Study of EPS Aggregate Insulation Material Used in Construction Sites

Online veröffentlicht: 10. Feb. 2024

Seitenbereich: 21 - 31

Eingereicht: 13. Apr. 2023

Akzeptiert: 22. Nov. 2023

DOI: https://doi.org/10.2478/rtuect-2024-0003

Schlüsselwörter
Drying, insulation material, recycled EPS, thermal conductivity

© 2024 Girts Bumanis et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.

Case Study of EPS Aggregate Insulation Material Used in Construction Sites

Online veröffentlicht: 10. Feb. 2024

Seitenbereich: 21 - 31

Eingereicht: 13. Apr. 2023

Akzeptiert: 22. Nov. 2023

DOI: https://doi.org/10.2478/rtuect-2024-0003

SchlüsselwörterDrying, insulation material, recycled EPS, thermal conductivity

© 2024 Girts Bumanis et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.

Schlüsselwörter
Drying, insulation material, recycled EPS, thermal conductivity