<abstract xmlns="http://www.w3.org/1999/xhtml">A novel 9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) graft γ-amino propyl triethoxy silane (KH550) was synthesized and introduced on the surface of wood fiber. Finally DOPO-g-KH550 treated wood fiber (DKTWF) was used to prepare DKTWF composite phenolic foams (DKTWFCPF). The structures of DOPO-g- KH550 was acknowledged by Fourier transform infrared (FT-IR) and nuclear magnetic resonance (1H-NMR). The structures of DKTWF were confirmed by FT-IR. Compared with wood fiber, the diffraction peaks’ position was basically unchanged, but the crystallinity was slightly increased and thermal stability were dramatically improved, T5% and Tmax increased by 21.9o and 36.1o respectively. But the char yield (800o) was slightly reduced. With the dosage of DKWF, there were different degrees of improvement including the mechanical properties, flame retardancy and microstructure of DKTWFCPF. Comprehensive analysis, the interfacial compatibility was significantly improved between DKTWF and phenolic resin, and the suitable content of DKTWF was 4%.</abstract>

A novel 9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) graft γ-amino propyl triethoxy silane (KH550) was synthesized and introduced on the surface of wood fiber. Finally DOPO-g-KH550 treated wood fiber (DKTWF) was used to prepare DKTWF composite phenolic foams (DKTWFCPF). The structures of DOPO-g- KH550 was acknowledged by Fourier transform infrared (FT-IR) and nuclear magnetic resonance (1H-NMR). The structures of DKTWF were confirmed by FT-IR. Compared with wood fiber, the diffraction peaks’ position was basically unchanged, but the crystallinity was slightly increased and thermal stability were dramatically improved, T5% and Tmax increased by 21.9o and 36.1o respectively. But the char yield (800o) was slightly reduced. With the dosage of DKWF, there were different degrees of improvement including the mechanical properties, flame retardancy and microstructure of DKTWFCPF. Comprehensive analysis, the interfacial compatibility was significantly improved between DKTWF and phenolic resin, and the suitable content of DKTWF was 4%.

A novel DOPO-g-KH550 modification wood fibers and its effects on the properties of composite phenolic foams

College of Materials Science and Engineering

Institute of Chemical Industry of Forestry Products, CAF

Polish Journal of Chemical Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

A novel 9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) graft γ-amino propyl triethoxy silane (KH550) was synthesized and introduced on the surface...

A novel DOPO-g-KH550 modification wood fibers and its effects on the properties of composite phenolic foams

Online veröffentlicht: 25. Juli 2018

Seitenbereich: 47 - 53

DOI: https://doi.org/10.2478/pjct-2018-0022

Schlüsselwörter
DOPO, Wood Fiber, Γ-amino propyl triethoxy silane, Composites, Characterization

© 2018 Yufeng Ma et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

A novel DOPO-g-KH550 modification wood fibers and its effects on the properties of composite phenolic foams

Online veröffentlicht: 25. Juli 2018

Seitenbereich: 47 - 53

DOI: https://doi.org/10.2478/pjct-2018-0022

SchlüsselwörterDOPO, Wood Fiber, Γ-amino propyl triethoxy silane, Composites, Characterization

© 2018 Yufeng Ma et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
DOPO, Wood Fiber, Γ-amino propyl triethoxy silane, Composites, Characterization