Areal weight | 600 g (±5%) |
Style/Pattern | Biax 0–90 – stitch |
Tensile strength | 3,500 (MPa) |
Tensile modulus | 72 (GPa) |
PC | 507.28 | 253.64 | 2.54 | 1,521.83 | 0 |
L18 | 507.28 | 253.64 | 2.54 | 1,369.65 | 61.46 |
L32 | 507.28 | 253.64 | 2.54 | 1,217.47 | 122.92 |
L45 | 507.28 | 253.64 | 2.54 | 1,065.28 | 184.38 |
L56 | 507.28 | 253.64 | 2.54 | 913.10 | 245.83 |
Cement | Density: 3.15 (g/cm3) | Type I blane fineness: 3,250 (kg/m2) |
Aggregates | Density: 2.6 (g/cm3) | Sand 4 mm |
EVA | Density: 0.55 (g/cm3) | 2–4 mm |
Water | Potable | |
Superplasticizer | Specific gravity (20°C): 1.069–1.109 (kg/l) | Polycarboxylic ether based |
Density (g/cm3) | 1.13–1.17 | 0.96–1.00 |
Viscosity (MPa) | 700–900 | 10–50 |
Epoxy equivalent (g/equivalent) | 166–182 | |
Epoxy value (value/100 g) | 0.55–0.60 | |
Refractor index | 1.5480–1.5530 | 1.5200–1.5210 |
Measurement conditions | 25°C | 25°C |
Flexural strength (MPa) | 110–140 | |
Modulus of elasticity (GPa) | 3.2–3.5 | |
Tensile strength (MPa) | 70–80 | |
Elongation at break (%) | 5.0–6.5 |
PC | 0 | – |
L18 | 18 | – |
L32 | 32 | – |
L45 | 45 | – |
L56 | 56 | – |
CPC | 0 | Coated |
CL18 | 18 | Coated |
CL32 | 32 | Coated |
CL45 | 45 | Coated |
CL56 | 56 | Coated |