<abstract xmlns="http://www.w3.org/1999/xhtml">

<p>The paper studies the effect of incorporating graphene oxide (GO) without surface functionalization on a commercial epoxy resin. GO was dispersed in a commercial epoxy resin at concentrations of 0 wt.%, 0.1 wt.%, 0.5 wt.%, 1 wt.%, and 3 wt.%. The resultant materials were deposited on carbon steel substrates, followed by the use of a 5 wt.% aqueous NaCl electrolyte, to evaluate the effectiveness of their anticorrosive coating function. Scanning electron microscopy (SEM) analysis showed that the GO was homogenously dispersed in the polymer matrix, resulting in flat and smooth surfaces. The X-ray diffraction (XRD) results showed that although GO was highly dispersed in the polymer matrix, multilayer graphene was also obtained after curing. The anticorrosive properties were evaluated by electrochemical impedance spectroscopy (EIS) at various exposure periods. Analysis of the prepared samples indicated that the best anticorrosion performance among them was available with the 0.5 wt.% GO coating. The obtained results indicate that GO–polymer matrix composites provide improved corrosion protection properties even after 500 h exposure to the NaCl solution.</p>
</abstract>

The paper studies the effect of incorporating graphene oxide (GO) without surface functionalization on a commercial epoxy resin. GO was dispersed in a commercial epoxy resin at concentrations of 0 wt.%, 0.1 wt.%, 0.5 wt.%, 1 wt.%, and 3 wt.%. The resultant materials were deposited on carbon steel substrates, followed by the use of a 5 wt.% aqueous NaCl electrolyte, to evaluate the effectiveness of their anticorrosive coating function. Scanning electron microscopy (SEM) analysis showed that the GO was homogenously dispersed in the polymer matrix, resulting in flat and smooth surfaces. The X-ray diffraction (XRD) results showed that although GO was highly dispersed in the polymer matrix, multilayer graphene was also obtained after curing. The anticorrosive properties were evaluated by electrochemical impedance spectroscopy (EIS) at various exposure periods. Analysis of the prepared samples indicated that the best anticorrosion performance among them was available with the 0.5 wt.% GO coating. The obtained results indicate that GO–polymer matrix composites provide improved corrosion protection properties even after 500 h exposure to the NaCl solution.

Effect of addition of non-functionalized graphene oxide in a commercial epoxy resin used as coating

Benemérita Universidad Autónoma de Puebla

Dirección de Innovación y Transferencia del Conocimiento

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

The paper studies the effect of incorporating graphene oxide (GO) without surface functionalization on a commercial epoxy resin. GO was dispersed in a...

Effect of addition of non-functionalized graphene oxide in a commercial epoxy resin used as coating

Online veröffentlicht: 01. März 2022

Seitenbereich: 467 - 477

Eingereicht: 18. Sept. 2021

Akzeptiert: 15. Dez. 2021

DOI: https://doi.org/10.2478/msp-2021-0039

Schlüsselwörter
epoxy, graphene oxide, nanocomposite coating, carbon steel, corrosion protection

© 2021 Jenaro Leocadio Varela Caselis et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Effect of addition of non-functionalized graphene oxide in a commercial epoxy resin used as coating

Online veröffentlicht: 01. März 2022

Seitenbereich: 467 - 477

Eingereicht: 18. Sept. 2021

Akzeptiert: 15. Dez. 2021

DOI: https://doi.org/10.2478/msp-2021-0039

Schlüsselwörterepoxy, graphene oxide, nanocomposite coating, carbon steel, corrosion protection

© 2021 Jenaro Leocadio Varela Caselis et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Schlüsselwörter
epoxy, graphene oxide, nanocomposite coating, carbon steel, corrosion protection