<abstract xmlns="http://www.w3.org/1999/xhtml">PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.</abstract>

PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Synthesis of single-crystalline Pb(Zr0.52Ti0.48)O3 nanocrystals by hydrothermal method

Department of Mechanical Science and Engineering

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Synthesis of single-crystalline Pb(ZrTi)O nanocrystals by hydrothermal method

PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and...

Synthesis of single-crystalline Pb(Zr_0.52Ti_0.48)O₃ nanocrystals by hydrothermal method

Online veröffentlicht: 18. Okt. 2019

Seitenbereich: 473 - 481

Eingereicht: 26. Okt. 2018

Akzeptiert: 03. Dez. 2018

DOI: https://doi.org/10.2478/msp-2019-0059

Schlüsselwörter
PbZrTiO nanocrystal, hydrothermal method, reaction temperature, reaction time, NaOH concentration

© 2019 Chunyu Deng et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Synthesis of single-crystalline Pb(Zr0.52Ti0.48)O3 nanocrystals by hydrothermal method

Online veröffentlicht: 18. Okt. 2019

Seitenbereich: 473 - 481

Eingereicht: 26. Okt. 2018

Akzeptiert: 03. Dez. 2018

DOI: https://doi.org/10.2478/msp-2019-0059

SchlüsselwörterPbZrTiO nanocrystal, hydrothermal method, reaction temperature, reaction time, NaOH concentration

© 2019 Chunyu Deng et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Synthesis of single-crystalline Pb(Zr_0.52Ti_0.48)O₃ nanocrystals by hydrothermal method

Schlüsselwörter
PbZrTiO nanocrystal, hydrothermal method, reaction temperature, reaction time, NaOH concentration