<abstract xmlns="http://www.w3.org/1999/xhtml">The effect of electrodeposition potential on the magnetic properties of the FeCoNi films has been reported in this paper. The FeCoNi electrodeposition was carried out from sulfate solution using potentiostatic technique. The obtained FeCoNi films were characterized by X-ray diffractometer (XRD), atomic absorption spectrometer (AAS) and vibrating sample magnetometer (VSM). It has been shown that the electrodeposition potential applied during the synthesis process determines the magnetic characteristics of FeCoNi films. The more negative potential is applied, the higher Ni content is in the FeCoNi alloy. At the same time, Co and Fe showed almost similar trend in which the content decreased with an increase in applied potential. The mean crystallite size of FeCoNi films was ranging from 11 nm to 15 nm. VSM evaluation indicated that the FeCoNi film is a ferromagnetic alloy with magnetic anisotropy. The high saturation magnetization of FeCoNi film was ranging from 86 A·m2/kg to 105 A·m2/kg. The film is a soft magnetic material which was revealed by a very low coercivity value in the range of 1.3 kA/m to 3.7 kA/m. Both the saturation magnetization and coercivity values decreased at a more negative electrodeposition potential.</abstract>

The effect of electrodeposition potential on the magnetic properties of the FeCoNi films has been reported in this paper. The FeCoNi electrodeposition was carried out from sulfate solution using potentiostatic technique. The obtained FeCoNi films were characterized by X-ray diffractometer (XRD), atomic absorption spectrometer (AAS) and vibrating sample magnetometer (VSM). It has been shown that the electrodeposition potential applied during the synthesis process determines the magnetic characteristics of FeCoNi films. The more negative potential is applied, the higher Ni content is in the FeCoNi alloy. At the same time, Co and Fe showed almost similar trend in which the content decreased with an increase in applied potential. The mean crystallite size of FeCoNi films was ranging from 11 nm to 15 nm. VSM evaluation indicated that the FeCoNi film is a ferromagnetic alloy with magnetic anisotropy. The high saturation magnetization of FeCoNi film was ranging from 86 A·m2/kg to 105 A·m2/kg. The film is a soft magnetic material which was revealed by a very low coercivity value in the range of 1.3 kA/m to 3.7 kA/m. Both the saturation magnetization and coercivity values decreased at a more negative electrodeposition potential.

Effect of the electrodeposition potential on the magnetic properties of FeCoNi films

Department of Chemistry, Faculty of Mathematics and Sciences

Department of Physics, Faculty of Mathematics and Natural Sciences

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The effect of electrodeposition potential on the magnetic properties of the FeCoNi films has been reported in this paper. The FeCoNi electrodeposition was...

Effect of the electrodeposition potential on the magnetic properties of FeCoNi films

Online veröffentlicht: 18. Okt. 2019

Seitenbereich: 389 - 394

Eingereicht: 07. Apr. 2018

Akzeptiert: 12. Nov. 2018

DOI: https://doi.org/10.2478/msp-2019-0044

Schlüsselwörter
magnetic properties, flexible substrate, soft magnetic film, electrodeposition potential, FeCoNi film

© 2019 Setia Budi et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Effect of the electrodeposition potential on the magnetic properties of FeCoNi films

Online veröffentlicht: 18. Okt. 2019

Seitenbereich: 389 - 394

Eingereicht: 07. Apr. 2018

Akzeptiert: 12. Nov. 2018

DOI: https://doi.org/10.2478/msp-2019-0044

Schlüsselwörtermagnetic properties, flexible substrate, soft magnetic film, electrodeposition potential, FeCoNi film

© 2019 Setia Budi et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
magnetic properties, flexible substrate, soft magnetic film, electrodeposition potential, FeCoNi film