<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Diamond-like carbon (DLC) films were electrochemically deposited onto indium tin oxide (ITO) substrates using acetic acid and deionized water as electrolyte at low deposition voltages (2.4 V and 60 V). The transmittance of the films was investigated by UV spectrometry. Transmittance measurements versus wavelength revealed that the films transmit 86 % to 89 % light in visible region and band gap of the films varies between 3.87 eV and 3.89 eV. Atomic force microscopy (AFM) and scanning electron microscopy (SEM) were used for structural characterization to evaluate surface morphology of the DLC films. The grain size and the surface roughness increased for the films prepared at higher deposition potential, while their measured average height decreased. The mechanical properties (hardness H and elastic modulus E<sub>r</sub>) were determined from load-displacement curves which were obtained by using nanoindentation method. Hardness and elastic modulus of the films increased as the deposition voltage of the films increased from 2.4 V to 60 V.</p></abstract>

Diamond-like carbon (DLC) films were electrochemically deposited onto indium tin oxide (ITO) substrates using acetic acid and deionized water as electrolyte at low deposition voltages (2.4 V and 60 V). The transmittance of the films was investigated by UV spectrometry. Transmittance measurements versus wavelength revealed that the films transmit 86 % to 89 % light in visible region and band gap of the films varies between 3.87 eV and 3.89 eV. Atomic force microscopy (AFM) and scanning electron microscopy (SEM) were used for structural characterization to evaluate surface morphology of the DLC films. The grain size and the surface roughness increased for the films prepared at higher deposition potential, while their measured average height decreased. The mechanical properties (hardness H and elastic modulus Er) were determined from load-displacement curves which were obtained by using nanoindentation method. Hardness and elastic modulus of the films increased as the deposition voltage of the films increased from 2.4 V to 60 V.

The effects of deposition potential on the optical, morphological and mechanical properties of DLC films produced by electrochemical deposition technique at low voltages

Department of Metallurgical and Materials Engineering

Depart. of Metallurgical and Materials Engineering

Department of Electrical and Electronics Engineering

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Diamond-like carbon (DLC) films were electrochemically deposited onto indium tin oxide (ITO) substrates using acetic acid and deionized water as electrolyte at...

The effects of deposition potential on the optical, morphological and mechanical properties of DLC films produced by electrochemical deposition technique at low voltages

Online veröffentlicht: 02. Aug. 2019

Seitenbereich: 166 - 172

Eingereicht: 12. Sept. 2017

Akzeptiert: 11. März 2019

DOI: https://doi.org/10.2478/msp-2019-0023

Schlüsselwörter
DLC films, optical properties, morphological properties, mechanical characterization

© 2019 Naim Aslan et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The effects of deposition potential on the optical, morphological and mechanical properties of DLC films produced by electrochemical deposition technique at low voltages

Online veröffentlicht: 02. Aug. 2019

Seitenbereich: 166 - 172

Eingereicht: 12. Sept. 2017

Akzeptiert: 11. März 2019

DOI: https://doi.org/10.2478/msp-2019-0023

SchlüsselwörterDLC films, optical properties, morphological properties, mechanical characterization

© 2019 Naim Aslan et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
DLC films, optical properties, morphological properties, mechanical characterization