<abstract xmlns="http://www.w3.org/1999/xhtml"> Tungsten trioxide (WO3) thin films were prepared by thermal evaporation technique on thoroughly cleaned glass substrates at high pressure of 133.322 mPa in presence of argon. The substrate temperature was maintained from 6 °C to 8 °C with the help of a cold jar. The deposited films were annealed at 400 °C in air for about 2 hours. The films were characterized in terms of their composition by X-ray photoelectron spectroscopy. Subsequently, the laboratory developed dry lithiation method was used to intercalate lithium atoms into as-deposited films in various proportions. With the amount of lithium content inserted into the film, the films showed coloration in visible and near infrared regions. The morphology, coloration efficiency and optical constants of annealed and lithiated films were calculated.</abstract>

Tungsten trioxide (WO3) thin films were prepared by thermal evaporation technique on thoroughly cleaned glass substrates at high pressure of 133.322 mPa in presence of argon. The substrate temperature was maintained from 6 °C to 8 °C with the help of a cold jar. The deposited films were annealed at 400 °C in air for about 2 hours. The films were characterized in terms of their composition by X-ray photoelectron spectroscopy. Subsequently, the laboratory developed dry lithiation method was used to intercalate lithium atoms into as-deposited films in various proportions. With the amount of lithium content inserted into the film, the films showed coloration in visible and near infrared regions. The morphology, coloration efficiency and optical constants of annealed and lithiated films were calculated.

Morphological, optical and electrochromic properties of dry-lithiated nanostructured WO3 thin films

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Morphological, optical and electrochromic properties of dry-lithiated nanostructured WO thin films

Tungsten trioxide (WO3) thin films were prepared by thermal evaporation technique on thoroughly cleaned glass substrates at high pressure of 133.322 mPa in...

Morphological, optical and electrochromic properties of dry-lithiated nanostructured WO₃ thin films

Online veröffentlicht: 25. Juni 2018

Seitenbereich: 341 - 347

Eingereicht: 01. Juni 2017

Akzeptiert: 27. März 2018

DOI: https://doi.org/10.2478/msp-2018-0048

Schlüsselwörter
WO3 thin films, thermal evaporation, XPS, atomic force microscopy, optical and electrochromic properties

© 2018 K.V. Madhuri and M. Bujji Babu, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Morphological, optical and electrochromic properties of dry-lithiated nanostructured WO3 thin films

Online veröffentlicht: 25. Juni 2018

Seitenbereich: 341 - 347

Eingereicht: 01. Juni 2017

Akzeptiert: 27. März 2018

DOI: https://doi.org/10.2478/msp-2018-0048

SchlüsselwörterWO3 thin films, thermal evaporation, XPS, atomic force microscopy, optical and electrochromic properties

© 2018 K.V. Madhuri and M. Bujji Babu, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Morphological, optical and electrochromic properties of dry-lithiated nanostructured WO₃ thin films

Schlüsselwörter
WO3 thin films, thermal evaporation, XPS, atomic force microscopy, optical and electrochromic properties