<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The paper presents an experimental study of five different gypsum composites taking into account paraffin permeability. The composites consist of synthetic gypsum, paraffin and polymers. The samples were produced from gypsum slurry of mixing ingredients, all in the liquid state. After 7 days of maturing, the condition of the samples was assessed as well as drying time was determined. In the second part, the paraffin tightness of different samples was analysed. The results showed that after three weeks of tests the tightness sample was A4. Other polymers were characterised by lower tightness. The content of polymer had also the effect on the final results, but the direct relation between polymer content and paraffin tightness was not observed.</p></abstract>

The paper presents an experimental study of five different gypsum composites taking into account paraffin permeability. The composites consist of synthetic gypsum, paraffin and polymers. The samples were produced from gypsum slurry of mixing ingredients, all in the liquid state. After 7 days of maturing, the condition of the samples was assessed as well as drying time was determined. In the second part, the paraffin tightness of different samples was analysed. The results showed that after three weeks of tests the tightness sample was A4. Other polymers were characterised by lower tightness. The content of polymer had also the effect on the final results, but the direct relation between polymer content and paraffin tightness was not observed.

Paraffin Permeability of Synthetic Gypsum Binders Modified by Individual Polymers

Latvian Journal of Physics and Technical Sciences

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The paper presents an experimental study of five different gypsum composites taking into account paraffin permeability. The composites consist of synthetic...

Paraffin Permeability of Synthetic Gypsum Binders Modified by Individual Polymers

Online veröffentlicht: 31. Dez. 2019

Seitenbereich: 47 - 56

DOI: https://doi.org/10.2478/lpts-2019-0034

Schlüsselwörter
admixture, gypsum, polymer, phase change materials, tightness

© 2019 K. Powała et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Paraffin Permeability of Synthetic Gypsum Binders Modified by Individual Polymers

Online veröffentlicht: 31. Dez. 2019

Seitenbereich: 47 - 56

DOI: https://doi.org/10.2478/lpts-2019-0034

Schlüsselwörteradmixture, gypsum, polymer, phase change materials, tightness

© 2019 K. Powała et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
admixture, gypsum, polymer, phase change materials, tightness