<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Within the national and international research program of materials for advanced nuclear reactors Czech organizations contributed with several tests of metallic alloys. The specimens of the alloys were first exposed in the long term (up to 1500 hours) in simulated advanced gas cooled reactor coolant environment at 750-900 °C. After exposure the degradation of tested materials was explored, especially changes in material microstructure, corrosion damage and corrosion layer composition and in some cases also changes in mechanical properties were observed. In this paper selected results of exposure tests in high temperature helium of alloy 800 H, austenitic steel 316L and high-temperature nickel alloys are presented.</p></abstract>

Within the national and international research program of materials for advanced nuclear reactors Czech organizations contributed with several tests of metallic alloys. The specimens of the alloys were first exposed in the long term (up to 1500 hours) in simulated advanced gas cooled reactor coolant environment at 750-900 °C. After exposure the degradation of tested materials was explored, especially changes in material microstructure, corrosion damage and corrosion layer composition and in some cases also changes in mechanical properties were observed. In this paper selected results of exposure tests in high temperature helium of alloy 800 H, austenitic steel 316L and high-temperature nickel alloys are presented.

High temperature alloys stability testing in impure helium

KOM – Corrosion and Material Protection Journal

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

{"article-title":"High temperature alloys stability testing in impure helium"}

Within the national and international research program of materials for advanced nuclear reactors Czech organizations contributed with several tests of...

High temperature alloys stability testing in impure helium

Online veröffentlicht: 16. Feb. 2018

Seitenbereich: 19 - 25

DOI: https://doi.org/10.2478/kom-2018-0004

© 2018 Berka J. et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.