<abstract xmlns="http://www.w3.org/1999/xhtml">

In this work, fluorine-doped tin oxide (FTO) and graphene/fluorine-doped (G-FTO) thin films were prepared using a low-cost spray pyrolysis method at a substrate temperature of 500 °C. For the FTOs, stannous chloride was dissolved in methanol and acetic acid to form the precursor solution. A 0.05 mole (M) of hydrofluoric acid was added to the precursor as an n-type impurity. The FTO thin film has an optical transmittance of 82% and electrical sheet resistance of 15 Ω/□. By meticulously integrating graphene into the optimal precursor solution of FTO, a significant improvement in the electrical conductivity of the prepared samples was achieved, leading to a reduction in the sheet resistance to 8 Ω/□ with a suitable optical transmittance of 79%. Structural, morphological, optical, and electrical properties of the prepared sample are investigated using X-ray diffraction, scanning electron microscope, UV spectroscopy, and four-point probe technique. The best performance of the FTO thin films is achieved utilizing 2.5 µmole/L of fluorine concentration at a substrate temperature of 500°C for a spraying exposer time of 20 min. The prepared sample has an electrical sheet resistance of 15 Ω/□, optical transmittance of 82%, and figure-of-merit of 91.2×10−4 Ω−1.The addition of 0.4 µmole/L of graphene to the optimum FTO samples enhances the performance by a remarkable reduction in the electrical the sheet resistance to 8 Ω/□ and an acceptable reduction in the optical transmittance of 79%. The overall value of the figure-of-merit increased to 118.3×10−4 Ω−1. The achieved results offer a high potential for adopting the prepared films for electronic and optoelectronic applications.
</abstract>

In this work, fluorine-doped tin oxide (FTO) and graphene/fluorine-doped (G-FTO) thin films were prepared using a low-cost spray pyrolysis method at a substrate temperature of 500 °C. For the FTOs, stannous chloride was dissolved in methanol and acetic acid to form the precursor solution. A 0.05 mole (M) of hydrofluoric acid was added to the precursor as an n-type impurity. The FTO thin film has an optical transmittance of 82% and electrical sheet resistance of 15 Ω/□. By meticulously integrating graphene into the optimal precursor solution of FTO, a significant improvement in the electrical conductivity of the prepared samples was achieved, leading to a reduction in the sheet resistance to 8 Ω/□ with a suitable optical transmittance of 79%. Structural, morphological, optical, and electrical properties of the prepared sample are investigated using X-ray diffraction, scanning electron microscope, UV spectroscopy, and four-point probe technique. The best performance of the FTO thin films is achieved utilizing 2.5 µmole/L of fluorine concentration at a substrate temperature of 500°C for a spraying exposer time of 20 min. The prepared sample has an electrical sheet resistance of 15 Ω/□, optical transmittance of 82%, and figure-of-merit of 91.2×10−4 Ω−1.The addition of 0.4 µmole/L of graphene to the optimum FTO samples enhances the performance by a remarkable reduction in the electrical the sheet resistance to 8 Ω/□ and an acceptable reduction in the optical transmittance of 79%. The overall value of the figure-of-merit increased to 118.3×10−4 Ω−1. The achieved results offer a high potential for adopting the prepared films for electronic and optoelectronic applications.

Preparation and characterization of graphene-based fluorine doped tin dioxide thin films via spray pyrolysis technique

Electrical Engineering Department, Faculty of Engineering

College of Engineering, Qassim University

Journal of Electrical Engineering

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

In this work, fluorine-doped tin oxide (FTO) and graphene/fluorine-doped (G-FTO) thin films were prepared using a low-cost spray pyrolysis method at a...

Preparation and characterization of graphene-based fluorine doped tin dioxide thin films via spray pyrolysis technique

Online veröffentlicht: 14. Dez. 2023

Seitenbereich: 463 - 473

Eingereicht: 12. Aug. 2023

DOI: https://doi.org/10.2478/jee-2023-0054

Schlüsselwörter
fluorine-doped tin-oxide, graphene/fluorine-doped tin-oxide, nebulizer spray pyrolysis technique, sheet resistance, transmittance

© 2023 Sherif A. Khaleel et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Preparation and characterization of graphene-based fluorine doped tin dioxide thin films via spray pyrolysis technique

Online veröffentlicht: 14. Dez. 2023

Seitenbereich: 463 - 473

Eingereicht: 12. Aug. 2023

DOI: https://doi.org/10.2478/jee-2023-0054

Schlüsselwörterfluorine-doped tin-oxide, graphene/fluorine-doped tin-oxide, nebulizer spray pyrolysis technique, sheet resistance, transmittance

© 2023 Sherif A. Khaleel et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Schlüsselwörter
fluorine-doped tin-oxide, graphene/fluorine-doped tin-oxide, nebulizer spray pyrolysis technique, sheet resistance, transmittance