<abstract xmlns="http://www.w3.org/1999/xhtml">The purpose of this study was to assess the effect on selected mechanical properties, of adding recast materials to the NiCrMo alloy of newly produced castings.Three groups of dental alloy NiCrMo (trade named Remanium CS+) were prepared by mixing 50% new alloy to alloy remnants from previous castings. The specimens in the first casting group used 100% new alloy and served as control (C1). The second group consisted of equal amounts of new alloy and alloy remnants cast only once (C2). The third group contained 50% of new alloy and alloy cast twice (C3). Microstructural analysis was performed and the chemical composition, hardness and the metal-ceramic bond strength were assessed. In addition, EDS analysis (mapping) was undertaken. Hardness and bond strength results were also statistically analysed.In spite of the fact that recasting brought about small changes in hardness and chemical composition (C, Cr and Mo), these effects were found to not affect their functional properties in the oral cavity. Still, significant differences between new alloy and the recasted groups (p &lt; 0.05) were demonstrated in the course of statistical analysis of Vickers hardness test (for α = 0.05). All analysed research groups have a similar average adhesion at 48.51÷49.24 MPa (p > 0.05).The recasting procedure described in the paper can be done safely in dentistry. If previously casted material is used, it should be mixed with new material. The use of the material prepared in this way can lower the costs of NiCrMo castings.</abstract>

The purpose of this study was to assess the effect on selected mechanical properties, of adding recast materials to the NiCrMo alloy of newly produced castings.Three groups of dental alloy NiCrMo (trade named Remanium CS+) were prepared by mixing 50% new alloy to alloy remnants from previous castings. The specimens in the first casting group used 100% new alloy and served as control (C1). The second group consisted of equal amounts of new alloy and alloy remnants cast only once (C2). The third group contained 50% of new alloy and alloy cast twice (C3). Microstructural analysis was performed and the chemical composition, hardness and the metal-ceramic bond strength were assessed. In addition, EDS analysis (mapping) was undertaken. Hardness and bond strength results were also statistically analysed.In spite of the fact that recasting brought about small changes in hardness and chemical composition (C, Cr and Mo), these effects were found to not affect their functional properties in the oral cavity. Still, significant differences between new alloy and the recasted groups (p < 0.05) were demonstrated in the course of statistical analysis of Vickers hardness test (for α = 0.05). All analysed research groups have a similar average adhesion at 48.51÷49.24 MPa (p > 0.05).The recasting procedure described in the paper can be done safely in dentistry. If previously casted material is used, it should be mixed with new material. The use of the material prepared in this way can lower the costs of NiCrMo castings.

Effect of addition of recast materials on characteristics of Ni-Cr-Mo alloys

Department of Transporting and Agricultural Machinery, Faculty of Production Engineering

Current Issues in Pharmacy and Medical Sciences

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

{"article-title":"Effect of addition of recast materials on characteristics of Ni-Cr-Mo alloys"}

The purpose of this study was to assess the effect on selected mechanical properties, of adding recast materials to the NiCrMo alloy of newly produced castings.Three groups of dental alloy NiCrMo (trade named Remanium CS+) were prepared by mixing 50% new alloy to alloy remnants from previous castings. The specimens in the first casting group used 100% new alloy and served as control (C1). The second group consisted of equal amounts of new alloy and alloy remnants cast only once (C2). The third group contained 50% of new alloy and alloy cast twice (C3). Microstructural analysis was performed and the chemical composition, hardness and the metal-ceramic bond strength were assessed. In addition, EDS analysis (mapping) was undertaken. Hardness and bond strength results were also statistically analysed.In spite of the fact that recasting brought about small changes in hardness and chemical composition (C, Cr and Mo), these effects were found to not affect their functional properties in the oral cavity. Still, significant differences between new alloy and the recasted groups (p  0.05).The recasting procedure described in the paper can be done safely in dentistry. If previously casted material is used, it should be mixed with new material. The use of the material prepared in this way can lower the costs of NiCrMo castings.

The purpose of this study was to assess the effect on selected mechanical properties, of adding recast materials to the NiCrMo alloy of newly produced...

Effect of addition of recast materials on characteristics of Ni-Cr-Mo alloys

Online veröffentlicht: 02. Juli 2019

Seitenbereich: 71 - 76

Eingereicht: 08. Juni 2018

Akzeptiert: 12. Okt. 2018

DOI: https://doi.org/10.2478/cipms-2019-0014

Schlüsselwörter
nickel alloys, metal-ceramic bonding, three-point bond test, recasting

© 2019 Mariusz Walczak et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Effect of addition of recast materials on characteristics of Ni-Cr-Mo alloys

Online veröffentlicht: 02. Juli 2019

Seitenbereich: 71 - 76

Eingereicht: 08. Juni 2018

Akzeptiert: 12. Okt. 2018

DOI: https://doi.org/10.2478/cipms-2019-0014

Schlüsselwörternickel alloys, metal-ceramic bonding, three-point bond test, recasting

© 2019 Mariusz Walczak et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
nickel alloys, metal-ceramic bonding, three-point bond test, recasting