<p>This research aims to produce a Compressed Earth Block (CEB) product using locally available soil collected from northern Jordan. The CEB mixture was further stabilized using Portland cement, lime, and sodium silicate. The research significance is based upon the urgent need of most developing countries (e.g. Jordan, Egypt…etc) to build more durable and low-cost houses by using locally available materials. As a result, CEB was identified as a cheap and environmentally friendly construction material. CEB specimens were thoroughly characterized by studying the mechanical properties and durability characteristics. Blocks of 30 x 15 x 8 cm with two holes of 7.5 cm in diameter have a potential for higher enduring, higher compressive strength, better thermal insulation, and lower production cost. Blocks were manufactured with an addition of 8 % for either Portland cement or lime, as well as 2 % of sodium silicate to the soil. The results showed that the addition of 8 % of cement to the CEB achieves satisfactory results in both mechanical and durability properties. Also, the addition of sodium silicate was found to enhance the early-age compressive strength however it affected negatively the durable properties of blocks by increasing the erosion rate and deterioration when exposed to water.</p>
</abstract>

This research aims to produce a Compressed Earth Block (CEB) product using locally available soil collected from northern Jordan. The CEB mixture was further stabilized using Portland cement, lime, and sodium silicate. The research significance is based upon the urgent need of most developing countries (e.g. Jordan, Egypt…etc) to build more durable and low-cost houses by using locally available materials. As a result, CEB was identified as a cheap and environmentally friendly construction material. CEB specimens were thoroughly characterized by studying the mechanical properties and durability characteristics. Blocks of 30 x 15 x 8 cm with two holes of 7.5 cm in diameter have a potential for higher enduring, higher compressive strength, better thermal insulation, and lower production cost. Blocks were manufactured with an addition of 8 % for either Portland cement or lime, as well as 2 % of sodium silicate to the soil. The results showed that the addition of 8 % of cement to the CEB achieves satisfactory results in both mechanical and durability properties. Also, the addition of sodium silicate was found to enhance the early-age compressive strength however it affected negatively the durable properties of blocks by increasing the erosion rate and deterioration when exposed to water.

Characteristics of Hollow Compressed Earth Block Stabilized Using Cement, Lime, and Sodium Silicate

Civil Engineering Department, Hijjawi Faculty for Engineering Technology

Civil and Environmental Engineering

This work is licensed under the Creative Commons Attribution 4.0 International License.

This research aims to produce a Compressed Earth Block (CEB) product using locally available soil collected from northern Jordan. The CEB mixture was further...

Characteristics of Hollow Compressed Earth Block Stabilized Using Cement, Lime, and Sodium Silicate

Online veröffentlicht: 22. Juni 2021

Seitenbereich: 200 - 208

DOI: https://doi.org/10.2478/cee-2021-0021

Schlüsselwörter
CEB, Cement, Lime, Sodium silicate, Stabilization

© 2021 Walid Edris et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.

Characteristics of Hollow Compressed Earth Block Stabilized Using Cement, Lime, and Sodium Silicate

Online veröffentlicht: 22. Juni 2021

Seitenbereich: 200 - 208

DOI: https://doi.org/10.2478/cee-2021-0021

SchlüsselwörterCEB, Cement, Lime, Sodium silicate, Stabilization

© 2021 Walid Edris et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.

Schlüsselwörter
CEB, Cement, Lime, Sodium silicate, Stabilization