<abstract xmlns="http://www.w3.org/1999/xhtml">

<p>In present study mass loss behaviour of base metal and heat-treated API X70 pipeline steel in different environments such as fresh water, sea water and sodium thiosulphate medium were observed for 50 days. Corrosion is the main failure in pipeline steel which need to be reduced with the use of suitable heat treatment process. In present study two heat treatment such as HT-1 900 °C (2 hour) with tempering at 450 °C (4 hour) and HT-2 800 °C (2 hour) with tempering at 450 °C (4 hour) was used. Mechanical, microstructure and corrosion rate of HT-1 and HT-2 specimen in different environments were observed. Maximum corrosion rate (0.306 mm/y) in fresh water while minimum corrosion rate (0.181 mm/y) in sodium thiosulphate medium was observed for base metal. Maximum corrosion rate (0.224 mm/y) in sodium thiosulphate while minimum corrosion rate (0.106 mm/y) in fresh water medium was observed for HT-1 specimen. For HT-2 specimen, Maximum corrosion rate (0.192 mm/y) in sea water while minimum corrosion rate (0.099 mm/y) in fresh water medium was observed. For HT-2 specimen, maximum average hardness of (30.3 HRC) in sea water while minimum average hardness of (28 HRC) of base metal was observed. In fresh water also HT-2 specimen, maximum average hardness is (26.3 HRC) while minimum average hardness of (24.6 HRC) of base metal was observed. After that maximum average hardness of base metal (26.6 HRC) in sodium thiosulphate while minimum average hardness of (21 HRC) of HT-2 specimen was observed.</p>
</abstract>

In present study mass loss behaviour of base metal and heat-treated API X70 pipeline steel in different environments such as fresh water, sea water and sodium thiosulphate medium were observed for 50 days. Corrosion is the main failure in pipeline steel which need to be reduced with the use of suitable heat treatment process. In present study two heat treatment such as HT-1 900 °C (2 hour) with tempering at 450 °C (4 hour) and HT-2 800 °C (2 hour) with tempering at 450 °C (4 hour) was used. Mechanical, microstructure and corrosion rate of HT-1 and HT-2 specimen in different environments were observed. Maximum corrosion rate (0.306 mm/y) in fresh water while minimum corrosion rate (0.181 mm/y) in sodium thiosulphate medium was observed for base metal. Maximum corrosion rate (0.224 mm/y) in sodium thiosulphate while minimum corrosion rate (0.106 mm/y) in fresh water medium was observed for HT-1 specimen. For HT-2 specimen, Maximum corrosion rate (0.192 mm/y) in sea water while minimum corrosion rate (0.099 mm/y) in fresh water medium was observed. For HT-2 specimen, maximum average hardness of (30.3 HRC) in sea water while minimum average hardness of (28 HRC) of base metal was observed. In fresh water also HT-2 specimen, maximum average hardness is (26.3 HRC) while minimum average hardness of (24.6 HRC) of base metal was observed. After that maximum average hardness of base metal (26.6 HRC) in sodium thiosulphate while minimum average hardness of (21 HRC) of HT-2 specimen was observed.

Experimental Investigation on Corrosion Behaviour of Heat-Treated API X70 Pipeline Steel

Research Scholar, Mechanical Engineering Department

Faculty of Mechanical Engineering Department

Faculty of Computer Science & Engineering Department

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

In present study mass loss behaviour of base metal and heat-treated API X70 pipeline steel in different environments such as fresh water, sea water and sodium...

Experimental Investigation on Corrosion Behaviour of Heat-Treated API X70 Pipeline Steel

Online veröffentlicht: 29. Juni 2024

Seitenbereich: 70 - 91

Eingereicht: 07. Feb. 2024

Akzeptiert: 20. Mai 2024

DOI: https://doi.org/10.2478/adms-2024-0013

Schlüsselwörter
Pipe line steel, Corrosion resistance, Heat treatment, Scanning electron microscope (SEM)

© 2024 Lochan Sharma et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Experimental Investigation on Corrosion Behaviour of Heat-Treated API X70 Pipeline Steel

Online veröffentlicht: 29. Juni 2024

Seitenbereich: 70 - 91

Eingereicht: 07. Feb. 2024

Akzeptiert: 20. Mai 2024

DOI: https://doi.org/10.2478/adms-2024-0013

SchlüsselwörterPipe line steel, Corrosion resistance, Heat treatment, Scanning electron microscope (SEM)

© 2024 Lochan Sharma et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
Pipe line steel, Corrosion resistance, Heat treatment, Scanning electron microscope (SEM)