<p>In this study, S235JR structural steel samples in uncoated condition and coated (shop-primer) in different thicknesses were welded by MAG (Metal Active Gas) welding method, and the effects of these applications on the mechanical and microstructure properties of the material were investigated. In the experimental studies, the first specimen group were used without any sandblasting and coating application, the second group specimens were sandblasted at Sa 2 ½ degree, and 25 µm, 50 µm, and 75 µm coatings were applied to the specimens in the other group. Surface conditions and coating thicknesses were selected as the variable parameters. With the examination of the radiography films, it was observed that the surface conditions affected the welded joint. As a result of the study, it was observed that altered coating thicknesses caused defects in the welding zone. It was determined that the coating thickness partially affected the mechanical properties, and the highest hardness values occurred in the weld zone in all samples. Relatively low values were obtained in tensile, bending and Charpy impact tests performed on sample groups with 75 µm coating thickness. The results were verified by the surface fracture, SEM, and EDS studies.</p>
</abstract>

In this study, S235JR structural steel samples in uncoated condition and coated (shop-primer) in different thicknesses were welded by MAG (Metal Active Gas) welding method, and the effects of these applications on the mechanical and microstructure properties of the material were investigated. In the experimental studies, the first specimen group were used without any sandblasting and coating application, the second group specimens were sandblasted at Sa 2 ½ degree, and 25 µm, 50 µm, and 75 µm coatings were applied to the specimens in the other group. Surface conditions and coating thicknesses were selected as the variable parameters. With the examination of the radiography films, it was observed that the surface conditions affected the welded joint. As a result of the study, it was observed that altered coating thicknesses caused defects in the welding zone. It was determined that the coating thickness partially affected the mechanical properties, and the highest hardness values occurred in the weld zone in all samples. Relatively low values were obtained in tensile, bending and Charpy impact tests performed on sample groups with 75 µm coating thickness. The results were verified by the surface fracture, SEM, and EDS studies.

Effect of Shop-Primer Coating on S235JR Steel on MAG Weldability

Faculty of Technology, Metallurgical and Materials Engineering Department

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Effect of Shop-Primer Coating on S235JR Steel on MAG Weldability"}

In this study, S235JR structural steel samples in uncoated condition and coated (shop-primer) in different thicknesses were welded by MAG (Metal Active Gas)...

Effect of Shop-Primer Coating on S235JR Steel on MAG Weldability

Online veröffentlicht: 12. Juli 2022

Seitenbereich: 49 - 63

DOI: https://doi.org/10.2478/adms-2022-0007

Schlüsselwörter
Sandblasting, surface coating, shop-primer, MAG welding, microstructure

© 2022 Cemil Çetinkaya et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Effect of Shop-Primer Coating on S235JR Steel on MAG Weldability

Online veröffentlicht: 12. Juli 2022

Seitenbereich: 49 - 63

DOI: https://doi.org/10.2478/adms-2022-0007

SchlüsselwörterSandblasting, surface coating, shop-primer, MAG welding, microstructure

© 2022 Cemil Çetinkaya et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
Sandblasting, surface coating, shop-primer, MAG welding, microstructure