<abstract xmlns="http://www.w3.org/1999/xhtml">

<p>This work reports a study of corrosion lifetime of transparent electrodes deposited on the microscopic glass substrate. A procedure was developed for obtaining the transparent electrode by spray method. The corrosion lifetime variation in the presence of 1.5 M NaOH medium chemically degraded at room temperature before and after gamma irradiation was determined by measuring the evolution of the structure, electrical and optical characteristics. The mean values of transmittance up to 25 month before and after irradiation were calculated 91% ±6% and 96±7%, respectively. The average value of resistivity after corrosion and age time after γ-irradiation was 0.016±9% Ω.cm and 0.017± 4% at 1.0 kHz. No significant changes observed for 27 hr corrosion and 25 month age time of the transparent electrodes in NaOH solution.</p>
</abstract>

This work reports a study of corrosion lifetime of transparent electrodes deposited on the microscopic glass substrate. A procedure was developed for obtaining the transparent electrode by spray method. The corrosion lifetime variation in the presence of 1.5 M NaOH medium chemically degraded at room temperature before and after gamma irradiation was determined by measuring the evolution of the structure, electrical and optical characteristics. The mean values of transmittance up to 25 month before and after irradiation were calculated 91% ±6% and 96±7%, respectively. The average value of resistivity after corrosion and age time after γ-irradiation was 0.016±9% Ω.cm and 0.017± 4% at 1.0 kHz. No significant changes observed for 27 hr corrosion and 25 month age time of the transparent electrodes in NaOH solution.

Corrosion of Transparent Electrodes Study

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Corrosion of Transparent Electrodes Study"}

This work reports a study of corrosion lifetime of transparent electrodes deposited on the microscopic glass substrate. A procedure was developed for obtaining...

Corrosion of Transparent Electrodes Study

Online veröffentlicht: 12. Juli 2022

Seitenbereich: 19 - 27

DOI: https://doi.org/10.2478/adms-2022-0005

Schlüsselwörter
electrodes, corrosion, γ-irradiation

© 2022 A. F. Maged et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Corrosion of Transparent Electrodes Study

Online veröffentlicht: 12. Juli 2022

Seitenbereich: 19 - 27

DOI: https://doi.org/10.2478/adms-2022-0005

Schlüsselwörterelectrodes, corrosion, γ-irradiation

© 2022 A. F. Maged et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
electrodes, corrosion, γ-irradiation