This study involves the effect of boriding powder composition on the microstructure and hardness of a CoCrMo alloy borided in a solid medium using the powder pack method. To investigate the effect of boriding powder composition, two different commercial boriding agents, Ekabor-HM and Ekabor III, were thoroughly mixed with ferrosilicon powders to form the boriding media. The CoCrMo samples were tightly packed with the Ekabor-HM and Ekabor III boriding powders in stainless steel containers to minimize oxidation. The boriding process was carried out under atmospheric conditions for 9 h in an electrical resistance furnace preheated to 1223 K. X-ray diffraction (XRD) analyses revealed that the surfaces of the borided CoCrMo alloys consisted of a bilayer composed of CoB and Co2B phases and also contained minor amounts of CrB, Mo2B5, and Mo2B. The average thickness of the boride layer in the samples borided with Ekabor HM and Ekabor III powders was 28±4.1 μm and 21±2.3 μm, while the average hardness of the boride layer was 1752±5.3 HV0.1 and 1364±3.8 HV0.1, respectively.
</abstract>

This study involves the effect of boriding powder composition on the microstructure and hardness of a CoCrMo alloy borided in a solid medium using the powder pack method. To investigate the effect of boriding powder composition, two different commercial boriding agents, Ekabor-HM and Ekabor III, were thoroughly mixed with ferrosilicon powders to form the boriding media. The CoCrMo samples were tightly packed with the Ekabor-HM and Ekabor III boriding powders in stainless steel containers to minimize oxidation. The boriding process was carried out under atmospheric conditions for 9 h in an electrical resistance furnace preheated to 1223 K. X-ray diffraction (XRD) analyses revealed that the surfaces of the borided CoCrMo alloys consisted of a bilayer composed of CoB and Co2B phases and also contained minor amounts of CrB, Mo2B5, and Mo2B. The average thickness of the boride layer in the samples borided with Ekabor HM and Ekabor III powders was 28±4.1 μm and 21±2.3 μm, while the average hardness of the boride layer was 1752±5.3 HV0.1 and 1364±3.8 HV0.1, respectively.

Microstructural Characterization of Borided Co-Cr-Mo Alloy

Süleyman Demirel University, Faculty of Arts and Sciences

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Microstructural Characterization of Borided Co-Cr-Mo Alloy"}

This study involves the effect of boriding powder composition on the microstructure and hardness of a CoCrMo alloy borided in a solid medium using the powder...

Microstructural Characterization of Borided Co-Cr-Mo Alloy

Online veröffentlicht: 30. Dez. 2021

Seitenbereich: 90 - 98

DOI: https://doi.org/10.2478/adms-2021-0027

Schlüsselwörter
Co-Cr-Mo alloy, boriding, coating, boride layer, hardness

© 2021 Nazim Ucar et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Microstructural Characterization of Borided Co-Cr-Mo Alloy

Online veröffentlicht: 30. Dez. 2021

Seitenbereich: 90 - 98

DOI: https://doi.org/10.2478/adms-2021-0027

SchlüsselwörterCo-Cr-Mo alloy, boriding, coating, boride layer, hardness

© 2021 Nazim Ucar et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
Co-Cr-Mo alloy, boriding, coating, boride layer, hardness