<p>This paper presents new results of studying the influence of parameters of microplasma spraying (MPS) of Zr wire on the structure of Zr coatings. The coating experiments were accomplished in a two level fractional factorial design. Individual particles of sprayed Zr wire and their splats on the substrate were collected under various spraying parameters (amperage, spraying distance, plasma gas flow rate and wire flow rate) and evaluated by Scanning Electron Microscopy (SEM) to establish the effect of particle size and shape on the coating microstructure. The particles were characterized by measurement of their sizes and the obtained results were evaluated in terms of their degree of melting. This was compared with the experimentally observed coating microstructure type and finally correlated to the investigated coating porosity to select the specific MPS parameters of Zr coatings depositing onto medical implants from Ti alloy. It was found that the main parameters influencing the size of the sprayed Zr particles and the porosity of the Zr coatings are the plasma gas flow rate and amperage. It was demonstrated that it is possible to control the porosity of Zr microplasma coatings in the range from 2.8% to 20.3% by changing the parameters of the MPS. The parameters of microplasma spraying of Zr wire were established to obtain medical implant coatings with porosity up to 20.3% and pore size up to 300 μm.</p>
</abstract>

This paper presents new results of studying the influence of parameters of microplasma spraying (MPS) of Zr wire on the structure of Zr coatings. The coating experiments were accomplished in a two level fractional factorial design. Individual particles of sprayed Zr wire and their splats on the substrate were collected under various spraying parameters (amperage, spraying distance, plasma gas flow rate and wire flow rate) and evaluated by Scanning Electron Microscopy (SEM) to establish the effect of particle size and shape on the coating microstructure. The particles were characterized by measurement of their sizes and the obtained results were evaluated in terms of their degree of melting. This was compared with the experimentally observed coating microstructure type and finally correlated to the investigated coating porosity to select the specific MPS parameters of Zr coatings depositing onto medical implants from Ti alloy. It was found that the main parameters influencing the size of the sprayed Zr particles and the porosity of the Zr coatings are the plasma gas flow rate and amperage. It was demonstrated that it is possible to control the porosity of Zr microplasma coatings in the range from 2.8% to 20.3% by changing the parameters of the MPS. The parameters of microplasma spraying of Zr wire were established to obtain medical implant coatings with porosity up to 20.3% and pore size up to 300 μm.

Fabrication and Characterization of Zr Microplasma Sprayed Coatings for Medical Applications

D. Serikbayev East Kazakhstan Technical University

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

This paper presents new results of studying the influence of parameters of microplasma spraying (MPS) of Zr wire on the structure of Zr coatings. The coating...

Fabrication and Characterization of Zr Microplasma Sprayed Coatings for Medical Applications

Online veröffentlicht: 01. Juli 2021

Seitenbereich: 93 - 105

DOI: https://doi.org/10.2478/adms-2021-0013

Schlüsselwörter
zirconium coatings, titanium implants, microplasma spraying (MPS), porosity, splats, scanning electron microscopy (SEM)

© 2021 Sergii G.Voinarovych et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Fabrication and Characterization of Zr Microplasma Sprayed Coatings for Medical Applications

Online veröffentlicht: 01. Juli 2021

Seitenbereich: 93 - 105

DOI: https://doi.org/10.2478/adms-2021-0013

Schlüsselwörterzirconium coatings, titanium implants, microplasma spraying (MPS), porosity, splats, scanning electron microscopy (SEM)

© 2021 Sergii G.Voinarovych et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
zirconium coatings, titanium implants, microplasma spraying (MPS), porosity, splats, scanning electron microscopy (SEM)