<abstract xmlns="http://www.w3.org/1999/xhtml"><p> Fracture evaluation of welded joints in high-strength steels, with bainitic and martensitic structures, is presented and cracking mechanisms discussed. Hot cracks or microcracks formed during welding are further expanded as cold cracks on cooling. The cause of cracking is shown to be low temperature of weld solidification and deformation-induced contraction. Hydrogen can also be an important factor in this cracking.</p></abstract>

Fracture evaluation of welded joints in high-strength steels, with bainitic and martensitic structures, is presented and cracking mechanisms discussed. Hot cracks or microcracks formed during welding are further expanded as cold cracks on cooling. The cause of cracking is shown to be low temperature of weld solidification and deformation-induced contraction. Hydrogen can also be an important factor in this cracking.

Cracking of High-Strength Steel Welded Joints

AGH University of Science and Technology, Faculty of Metals Engineering and Industrial Computer Science, Department of Physical and Powder Metallurgy, 30-059 Cracow, Poland

Advances in Materials Science

{"article-title":"Cracking of High-Strength Steel Welded Joints"}

Fracture evaluation of welded joints in high-strength steels, with bainitic and martensitic structures, is presented and cracking mechanisms discussed. Hot...

Cracking of High-Strength Steel Welded Joints

Online veröffentlicht: 15. Okt. 2013

Seitenbereich: 76 - 85

DOI: https://doi.org/10.2478/adms-2013-0013

This content is open access.