<abstract xmlns="http://www.w3.org/1999/xhtml"> The TiO2 electrode has a key role in dye sensitized solar cell (DSSC) technology in the charge generation and charge transportation. The properties of TiO2 layer affect resulting efficiency of DSSC and can be controlled by printing process and chemical composition of printing paste. TiO2 pastes with different compositions of TiO2 nanoparticles, ethanol, ethyl cellulose, water, acetic acid, α-terpineol were prepared and screen printed onto the glass substrate with fluorine doped tin oxide (FTO). The TiO2 pastes for screen printing were characterized by rheological measurements and screen printed TiO2 electrodes by atomic force microscopy and UV-Vis spectroscopy. The photocurrent - voltage characteristics and efficiencies of DSSC were evaluated and compared. All prepared TiO2 pastes were suitable for screen printing with ideal rheological characteristics. The highest efficiency 0.68 % and current density ISC = 1.21 mA/cm2 reached by the DSSC based on TiO2 electrode with thickness 1.5 μm, with amount of absorbed dye 1.1 × 10-8 mol/cm2 and without visible cracks and particles aggregation. This TiO2 electrode was prepared from the paste containing 5.4 wt. % of TiO2, 65.3 wt. % of ethanol, 1.8 wt. % of ethyl cellulose, 23 wt. % of H2O and 4.5 wt. % of CH3COOH.</abstract>

The TiO2 electrode has a key role in dye sensitized solar cell (DSSC) technology in the charge generation and charge transportation. The properties of TiO2 layer affect resulting efficiency of DSSC and can be controlled by printing process and chemical composition of printing paste. TiO2 pastes with different compositions of TiO2 nanoparticles, ethanol, ethyl cellulose, water, acetic acid, α-terpineol were prepared and screen printed onto the glass substrate with fluorine doped tin oxide (FTO). The TiO2 pastes for screen printing were characterized by rheological measurements and screen printed TiO2 electrodes by atomic force microscopy and UV-Vis spectroscopy. The photocurrent - voltage characteristics and efficiencies of DSSC were evaluated and compared. All prepared TiO2 pastes were suitable for screen printing with ideal rheological characteristics. The highest efficiency 0.68 % and current density ISC = 1.21 mA/cm2 reached by the DSSC based on TiO2 electrode with thickness 1.5 μm, with amount of absorbed dye 1.1 × 10-8 mol/cm2 and without visible cracks and particles aggregation. This TiO2 electrode was prepared from the paste containing 5.4 wt. % of TiO2, 65.3 wt. % of ethanol, 1.8 wt. % of ethyl cellulose, 23 wt. % of H2O and 4.5 wt. % of CH3COOH.

Effi ciency of dye sensitized solar cells with various compositions of TiO2 based screen printed photoactive electrodes

Slovak University of Technology in Bratislava, Faculty of Chemical and Food Technology, Department of Graphic Art Technology and Applied Photochemistry, Radlinského 9, 821 37, Bratislava, Slovakia

Acta Chimica Slovaca

The TiO2 electrode has a key role in dye sensitized solar cell (DSSC) technology in the charge generation and charge transportation. The properties of TiO2...

Effi ciency of dye sensitized solar cells with various compositions of TiO2 based screen printed photoactive electrodes

Online veröffentlicht: 22. Mai 2013

Seitenbereich: 29 - 34

DOI: https://doi.org/10.2478/acs-2013-0006

Schlüsselwörter
TiO2 nanoporous electrode, dye sensitized solar cell, screen printing

This content is open access.

Effi ciency of dye sensitized solar cells with various compositions of TiO2 based screen printed photoactive electrodes

Online veröffentlicht: 22. Mai 2013

Seitenbereich: 29 - 34

DOI: https://doi.org/10.2478/acs-2013-0006

SchlüsselwörterTiO2 nanoporous electrode, dye sensitized solar cell, screen printing

This content is open access.

Schlüsselwörter
TiO2 nanoporous electrode, dye sensitized solar cell, screen printing