<abstract xmlns="http://www.w3.org/1999/xhtml"><sec><h3>Aim</h3><p>The objective of the present study was to determine which of six bonding protocols yielded a clinically acceptable shear bond strength (SBS) of metal orthodontic brackets to CAD/CAM lithium disilicate porcelain restorations. A secondary aim was to determine which bonding protocol produced the least surface damage at debond.</p></sec><sec><h3>Methods</h3><p>Sixty lithium disilicate samples were fabricated to replicate the facial surface of a mandibular first molar using a CEREC CAD/CAM machine. The samples were split into six test groups, each of which received different mechanical/chemical pretreatment protocols to roughen the porcelain surface prior to bonding a molar orthodontic attachment. Shear bond strength testing was conducted using an Instron machine. The mean, maximum, minimal, and standard deviation SBS values for each sample group including an enamel control were calculated. A <italic>t</italic>-test was used to evaluate the statistical significance between the groups.</p></sec><sec><h3>Results</h3><p>No significant differences were found in SBS values, with the exception of surface roughening with a green stone prior to HFA and silane treatment. This protocol yielded slightly higher bond strength which was statistically significant.</p></sec><sec><h3>Conclusion</h3><p>Chemical treatment alone with HFA/silane yielded SBS values within an acceptable clinical range to withstand forces applied by orthodontic treatment and potentially eliminates the need to mechanically roughen the ceramic surface.</p></sec></abstract>

AimThe objective of the present study was to determine which of six bonding protocols yielded a clinically acceptable shear bond strength (SBS) of metal orthodontic brackets to CAD/CAM lithium disilicate porcelain restorations. A secondary aim was to determine which bonding protocol produced the least surface damage at debond.MethodsSixty lithium disilicate samples were fabricated to replicate the facial surface of a mandibular first molar using a CEREC CAD/CAM machine. The samples were split into six test groups, each of which received different mechanical/chemical pretreatment protocols to roughen the porcelain surface prior to bonding a molar orthodontic attachment. Shear bond strength testing was conducted using an Instron machine. The mean, maximum, minimal, and standard deviation SBS values for each sample group including an enamel control were calculated. A t-test was used to evaluate the statistical significance between the groups.ResultsNo significant differences were found in SBS values, with the exception of surface roughening with a green stone prior to HFA and silane treatment. This protocol yielded slightly higher bond strength which was statistically significant.ConclusionChemical treatment alone with HFA/silane yielded SBS values within an acceptable clinical range to withstand forces applied by orthodontic treatment and potentially eliminates the need to mechanically roughen the ceramic surface.

Porcelain surface conditioning protocols and shear bond strength of orthodontic brackets

Australasian Orthodontic Journal

This work is licensed under the Creative Commons Attribution 4.0 International License.

AimThe objective of the present study was to determine which of six bonding protocols yielded a clinically acceptable shear bond strength (SBS) of metal...

Porcelain surface conditioning protocols and shear bond strength of orthodontic brackets

Online veröffentlicht: 30. Juli 2021

Seitenbereich: 18 - 22

Eingereicht: 01. Mai 2015

Akzeptiert: 01. Jan. 2016

DOI: https://doi.org/10.21307/aoj-2020-108

© 2016 Ashley M. Lestrade et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.