<abstract xmlns="http://www.w3.org/1999/xhtml">The influence of organic additives on the process of surface electropolishing of AISI 304 type steel was determined. Additives were selected in initial potentiodynamic tests pursuant to the plateau analysis on the current/potential curves. The assessment of the operational effectiveness of additives consisted in determining the relationship between surface gloss after electropolishing and the mass loss of the sample and in determining surface roughness. The applied electropolishing bath consisted of a mixture of concentrated acids: H3PO4 and H2SO4, and the following organic additives were used: triethylamine, ethanolamine, diethanolamine, triethanolamine, diethylene glycol monobutyl ether and glycerol. The best electropolishing result, i.e. low roughness and high gloss of stainless steel surface with a relatively low mass loss of the sample at the same time were obtained for baths containing triethanolamine.</abstract>

The influence of organic additives on the process of surface electropolishing of AISI 304 type steel was determined. Additives were selected in initial potentiodynamic tests pursuant to the plateau analysis on the current/potential curves. The assessment of the operational effectiveness of additives consisted in determining the relationship between surface gloss after electropolishing and the mass loss of the sample and in determining surface roughness. The applied electropolishing bath consisted of a mixture of concentrated acids: H3PO4 and H2SO4, and the following organic additives were used: triethylamine, ethanolamine, diethanolamine, triethanolamine, diethylene glycol monobutyl ether and glycerol. The best electropolishing result, i.e. low roughness and high gloss of stainless steel surface with a relatively low mass loss of the sample at the same time were obtained for baths containing triethanolamine.

Improvement of the stainless steel electropolishing process by organic additives

Wroclaw University of Environmental and Life Sciences, Institute of Environmental Engineering, pl. Grunwaldzki 24a, 50-365 Wrocław,

Wroclaw University of Science and Technology, Department of Machine Tools and Mechanical Technologies, Łukasiewicza 5, 50-370 Wrocław,

Wroclaw University of Science and Technology, Department of Advanced Material Technologies, Smoluchowskiego 21, 50-372 Wrocław,

Polish Journal of Chemical Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Improvement of the stainless steel electropolishing process by organic additives"}

The influence of organic additives on the process of surface electropolishing of AISI 304 type steel was determined. Additives were selected in initial...

Improvement of the stainless steel electropolishing process by organic additives

Online veröffentlicht: 30. Dez. 2016

Seitenbereich: 76 - 81

DOI: https://doi.org/10.1515/pjct-2016-0074

Schlüsselwörter
electropolishing, organic additives, surface roughness, stainless steel

© 2016 Pawel Lochynski et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Improvement of the stainless steel electropolishing process by organic additives

Online veröffentlicht: 30. Dez. 2016

Seitenbereich: 76 - 81

DOI: https://doi.org/10.1515/pjct-2016-0074

Schlüsselwörterelectropolishing, organic additives, surface roughness, stainless steel

© 2016 Pawel Lochynski et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
electropolishing, organic additives, surface roughness, stainless steel