<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>This paper describes behaviour of the ferritic-martensitic steel T91 after long-term exposure in liquid eutectic PbBi. Small specimens of the steel were pre-loaded according to the ISO Standard No. 7539-2 and subsequently exposed to PbBi. The experiment was carried out in a flowing and static liquid metal medium at 350°C. The experimental time was selected for the flowing environment at 1000 hours and for static environment at 2000 hours. After exposure, the specimens were analysed by use SEM and EDX. Surface changes of the specimens from different experimental conditions were compared and discussed. The initiation of the cracks wasn´t observed in the monitored expositions.</p></abstract>

This paper describes behaviour of the ferritic-martensitic steel T91 after long-term exposure in liquid eutectic PbBi. Small specimens of the steel were pre-loaded according to the ISO Standard No. 7539-2 and subsequently exposed to PbBi. The experiment was carried out in a flowing and static liquid metal medium at 350°C. The experimental time was selected for the flowing environment at 1000 hours and for static environment at 2000 hours. After exposure, the specimens were analysed by use SEM and EDX. Surface changes of the specimens from different experimental conditions were compared and discussed. The initiation of the cracks wasn´t observed in the monitored expositions.

Analysis of resistance of T91 steel under load in liquid PbBi

Koroze a ochrana materiálu

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

{"article-title":"Analysis of resistance of T91 steel under load in liquid PbBi"}

This paper describes behaviour of the ferritic-martensitic steel T91 after long-term exposure in liquid eutectic PbBi. Small specimens of the steel were...

Analysis of resistance of T91 steel under load in liquid PbBi

Online veröffentlicht: 11. Jan. 2018

Seitenbereich: 185 - 190

DOI: https://doi.org/10.1515/kom-2017-0024

© by L. Rozumová

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.