<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Mixed oxide-based pigments Mg–Zn–Fe with different particle morphologies were prepared by high-temperature solid phase reactions. The core shell pigments containing ferric oxide and non-isometric particles of layered silicates were also prepared. The pigments were tested in paints, the pigment volume concentrations in the modified alkyd resin based binder being 5%, 10%, and 15%. The paint properties were examined by accelerated corrosion tests and by physico-mechanical tests. The effect of the pigment particle morphology on the surface hardness of the paint films was also studied. The influence of pigment volume concentration on the coating properties, and the optimum concentrations providing the most efficient anticorrosive protection were processed. A higher anticorrosion efficiency was observed for the paints with pigments possessing the lamellar particle shape.</p></abstract>

Mixed oxide-based pigments Mg–Zn–Fe with different particle morphologies were prepared by high-temperature solid phase reactions. The core shell pigments containing ferric oxide and non-isometric particles of layered silicates were also prepared. The pigments were tested in paints, the pigment volume concentrations in the modified alkyd resin based binder being 5%, 10%, and 15%. The paint properties were examined by accelerated corrosion tests and by physico-mechanical tests. The effect of the pigment particle morphology on the surface hardness of the paint films was also studied. The influence of pigment volume concentration on the coating properties, and the optimum concentrations providing the most efficient anticorrosive protection were processed. A higher anticorrosion efficiency was observed for the paints with pigments possessing the lamellar particle shape.

Anticorrosive efficiency of alkyd resin-based coatings containing Mg–Zn–Fe mixed oxide-based pigments

University of Pardubice, Faculty of Chemical Technology, Institute of Chemistry and Material Technology, Department of Painting and Organic Coatings

KOM – Corrosion and Material Protection Journal

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Mixed oxide-based pigments Mg–Zn–Fe with different particle morphologies were prepared by high-temperature solid phase reactions. The core shell pigments...

Anticorrosive efficiency of alkyd resin-based coatings containing Mg–Zn–Fe mixed oxide-based pigments

Online veröffentlicht: 20. März 2017

Seitenbereich: 39 - 53

DOI: https://doi.org/10.1515/kom-2017-0005

© 2017 Kalendová A. et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.