<abstract xmlns="http://www.w3.org/1999/xhtml"><p> Objectives. The objective of the research was to define the mechanical properties of currently marketed temporary filling materials. Methods. Eight temporary filling materials: Boston, Dentalon, Protemp II, Revotek LC, Structure 2, Structure 3, UniFast LC, UniFast Trad were used to make 5 samples each of measurements 2 × 2 × 25 mm, in order to define the flexural strength, and 10 rings each of measurements 2 × 5 mm, in order to carry out the Vickers micro-hardness test. After preparation, the samples were stored in distilled water of temperature of 370°C, for 7 days. Subsequently, flexural strength and Vickers hardness testing was undertaken. Results. Composite temporary materials showed considerably better mechanical properties, both in flexural strength and in Vickers micro-hardness testing. Conclusions. the best mechanical properties, both in terms of flexural strength, as well as Vickers micro-hardness test can be observe among composite materials.</p></abstract>

Objectives. The objective of the research was to define the mechanical properties of currently marketed temporary filling materials. Methods. Eight temporary filling materials: Boston, Dentalon, Protemp II, Revotek LC, Structure 2, Structure 3, UniFast LC, UniFast Trad were used to make 5 samples each of measurements 2 × 2 × 25 mm, in order to define the flexural strength, and 10 rings each of measurements 2 × 5 mm, in order to carry out the Vickers micro-hardness test. After preparation, the samples were stored in distilled water of temperature of 370°C, for 7 days. Subsequently, flexural strength and Vickers hardness testing was undertaken. Results. Composite temporary materials showed considerably better mechanical properties, both in flexural strength and in Vickers micro-hardness testing. Conclusions. the best mechanical properties, both in terms of flexural strength, as well as Vickers micro-hardness test can be observe among composite materials.

Mechanical properties of materials used for temporary fixed dentures – in vitro study

Current Issues in Pharmacy and Medical Sciences

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Objectives. The objective of the research was to define the mechanical properties of currently marketed temporary filling materials. Methods. Eight temporary...

Mechanical properties of materials used for temporary fixed dentures – in vitro study

Online veröffentlicht: 25. Okt. 2017

Seitenbereich: 61 - 64

Eingereicht: 01. März 2017

Akzeptiert: 26. Mai 2017

DOI: https://doi.org/10.1515/cipms-2017-0012

Schlüsselwörter
dental materials, provisional materials, flexural strength, hardness

© 2017

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Mechanical properties of materials used for temporary fixed dentures – in vitro study

Online veröffentlicht: 25. Okt. 2017

Seitenbereich: 61 - 64

Eingereicht: 01. März 2017

Akzeptiert: 26. Mai 2017

DOI: https://doi.org/10.1515/cipms-2017-0012

Schlüsselwörterdental materials, provisional materials, flexural strength, hardness

© 2017

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
dental materials, provisional materials, flexural strength, hardness