<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Research and development activities presented were aimed at obtaining a nanocomposite polyurethane matrix with special anti-wear, anti-slip and fire-resistant properties. Research and development works were materialized by obtaining polyurethane nanocomposite matrix, by its physico-chemical modification in order to give the desired technological properties and by characterization of the obtained material. Polyurethane nanocomposite matrix was obtained by reacting a PETOL 3 type polyetherpolyol (having a molecular weight of 5000 UAM) with a diisocyanate under well-established reaction conditions. Target specific technological properties were obtained by physical and chemical modification of polyurethane nanocomposite matrix. The final result was getting a pellicle material based on modified nanocomposite polyurethane, with anti-wear, anti-slip and fire-resistant properties, compatible with most substrates encountered in civil and industrial construction: wood, concrete, metal.</p></abstract>

Research and development activities presented were aimed at obtaining a nanocomposite polyurethane matrix with special anti-wear, anti-slip and fire-resistant properties. Research and development works were materialized by obtaining polyurethane nanocomposite matrix, by its physico-chemical modification in order to give the desired technological properties and by characterization of the obtained material. Polyurethane nanocomposite matrix was obtained by reacting a PETOL 3 type polyetherpolyol (having a molecular weight of 5000 UAM) with a diisocyanate under well-established reaction conditions. Target specific technological properties were obtained by physical and chemical modification of polyurethane nanocomposite matrix. The final result was getting a pellicle material based on modified nanocomposite polyurethane, with anti-wear, anti-slip and fire-resistant properties, compatible with most substrates encountered in civil and industrial construction: wood, concrete, metal.

Physical Training Methods For Mine Rescuers In 2015

Faculty of Real Sciences, Department of Physical and Engineering Sciences, AlecuRussoBalti State University, Puskin38, Balti, Moldova

National Institute for Research and Development in Chemistry and Petrochemistry, Polymer Department, Spl. Independentei 202, Bucharest, Romania

Acta Universitatis Cibiniensis. Technical Series

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Physical Training Methods For Mine Rescuers In 2015"}

Research and development activities presented were aimed at obtaining a nanocomposite polyurethane matrix with special anti-wear, anti-slip and fire-resistant...

Physical Training Methods For Mine Rescuers In 2015

Online veröffentlicht: 23. Sept. 2015

Seitenbereich: 108 - 113

DOI: https://doi.org/10.1515/aucts-2015-0037

Schlüsselwörter
polyurethane, nanocomposite, antiwear, antislip, fire resistant

© Marin Laurentiu et al.

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Physical Training Methods For Mine Rescuers In 2015

Online veröffentlicht: 23. Sept. 2015

Seitenbereich: 108 - 113

DOI: https://doi.org/10.1515/aucts-2015-0037

Schlüsselwörterpolyurethane, nanocomposite, antiwear, antislip, fire resistant

© Marin Laurentiu et al.

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
polyurethane, nanocomposite, antiwear, antislip, fire resistant