<abstract xmlns="http://www.w3.org/1999/xhtml">The high-speed steel HS 6-5-2 cutting inserts coated with TiN were subjected to ion implantation with both silicon (dose 2×1017Si+/cm2) and silicon with nitrogen ions (dose (1+1)×1017(Si+ + N+)/cm2) on the subsurface layer of the rake face. Microhardness was examined before and after ion implantation. The composition and structural properties of the subsurface layer were examined by Glow Discharge Optical Emission Spectroscopy (GD-OES). The turning tests of 40H construction steel with the use of the cutting inserts implanted and non-implanted were performed. During the tests the two components of the net cutting force (the main cutting force Fc and feed force Ff) as well as the wear parameters VB on the major flankalong with the surface roughness (Ra) were measured. The implanted inserts exhibited higher durability compared to non-implanted ones.</abstract>

The high-speed steel HS 6-5-2 cutting inserts coated with TiN were subjected to ion implantation with both silicon (dose 2×1017Si+/cm2) and silicon with nitrogen ions (dose (1+1)×1017(Si+ + N+)/cm2) on the subsurface layer of the rake face. Microhardness was examined before and after ion implantation. The composition and structural properties of the subsurface layer were examined by Glow Discharge Optical Emission Spectroscopy (GD-OES). The turning tests of 40H construction steel with the use of the cutting inserts implanted and non-implanted were performed. During the tests the two components of the net cutting force (the main cutting force Fc and feed force Ff) as well as the wear parameters VB on the major flankalong with the surface roughness (Ra) were measured. The implanted inserts exhibited higher durability compared to non-implanted ones.

Modification of TiN coatings by Ion Implantation

Kazimierz Pułaski University of Technology and Humanities

Acta Mechanica et Automatica

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

{"article-title":"Modification of TiN coatings by Ion Implantation"}

The high-speed steel HS 6-5-2 cutting inserts coated with TiN were subjected to ion implantation with both silicon (dose 2×1017Si+/cm2) and silicon with...

Modification of TiN coatings by Ion Implantation

Online veröffentlicht: 07. Okt. 2017

Seitenbereich: 190 - 193

Eingereicht: 11. Jan. 2016

Akzeptiert: 09. Aug. 2017

DOI: https://doi.org/10.1515/ama-2017-0028

Schlüsselwörter
Ion Implantation, TiN, Silicon, HSS, Turning

© 2017 Jerzy Narojczyk et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Modification of TiN coatings by Ion Implantation

Online veröffentlicht: 07. Okt. 2017

Seitenbereich: 190 - 193

Eingereicht: 11. Jan. 2016

Akzeptiert: 09. Aug. 2017

DOI: https://doi.org/10.1515/ama-2017-0028

SchlüsselwörterIon Implantation, TiN, Silicon, HSS, Turning

© 2017 Jerzy Narojczyk et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
Ion Implantation, TiN, Silicon, HSS, Turning