<abstract xmlns="http://www.w3.org/1999/xhtml"> The SEM and EDS results of coatings obtained on pure niobium and titanium alloys (NiTi and Ti6Al4V) by Plasma Electrolytic Oxidation in the electrolytes containing of 300 g and 600 g copper nitrate in 1 litre of concentrated phosphoric acid at 450 V for 3 minutes, are presented. The obtained coatings are porous and consist mainly of phosphorus within titanium and copper. For each coating, the Cu/P ratios were calculated. The maximum of that coefficient was found for niobium and Ti6Al4V alloy oxidised in the electrolyte containing 600 g of Cu(NO3)2 in 1 dm3 of H3PO4 and equaling to 0.22 (wt%) | 0.11 (at%). The minimum of Cu/P ratio was recorded for NiTi and Ti6Al4V alloys oxidised by PEO in electrolyte consisting of 300 g of copper nitrate in 1 dm3 of concentrated phosphoric acid and equals to 0.12 (wt%) | 0.06 (at%). The middle value of that ratio was recorded for NiTi and it equals to 0.16 (wt%) | 0.08 (at%).</abstract>

The SEM and EDS results of coatings obtained on pure niobium and titanium alloys (NiTi and Ti6Al4V) by Plasma Electrolytic Oxidation in the electrolytes containing of 300 g and 600 g copper nitrate in 1 litre of concentrated phosphoric acid at 450 V for 3 minutes, are presented. The obtained coatings are porous and consist mainly of phosphorus within titanium and copper. For each coating, the Cu/P ratios were calculated. The maximum of that coefficient was found for niobium and Ti6Al4V alloy oxidised in the electrolyte containing 600 g of Cu(NO3)2 in 1 dm3 of H3PO4 and equaling to 0.22 (wt%) | 0.11 (at%). The minimum of Cu/P ratio was recorded for NiTi and Ti6Al4V alloys oxidised by PEO in electrolyte consisting of 300 g of copper nitrate in 1 dm3 of concentrated phosphoric acid and equals to 0.12 (wt%) | 0.06 (at%). The middle value of that ratio was recorded for NiTi and it equals to 0.16 (wt%) | 0.08 (at%).

Characterization of Coatings Created on Selected Titanium Alloys by Plasma Electrolytic Oxidation

Koszalin University of Technology, Faculty of Mechanical Engineering, Division of Surface Electrochemistry, Racławicka 15-17, 75-620 Koszalin, Poland

Hochschule Wismar-University of Applied Sciences Technology, Business and Design, Faculty of Engineering, DE 23966 Wismar, Germany

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The SEM and EDS results of coatings obtained on pure niobium and titanium alloys (NiTi and Ti6Al4V) by Plasma Electrolytic Oxidation in the electrolytes...

Characterization of Coatings Created on Selected Titanium Alloys by Plasma Electrolytic Oxidation

Online veröffentlicht: 29. Apr. 2016

Seitenbereich: 5 - 16

DOI: https://doi.org/10.1515/adms-2016-0001

Schlüsselwörter
Plasma Electrolytic Oxidation, PEO, Micro Arc Oxidation, MAO, SEM, Titanium alloy, NiTi

© by K. Rokosz

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Characterization of Coatings Created on Selected Titanium Alloys by Plasma Electrolytic Oxidation

Online veröffentlicht: 29. Apr. 2016

Seitenbereich: 5 - 16

DOI: https://doi.org/10.1515/adms-2016-0001

SchlüsselwörterPlasma Electrolytic Oxidation, PEO, Micro Arc Oxidation, MAO, SEM, Titanium alloy, NiTi

© by K. Rokosz

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
Plasma Electrolytic Oxidation, PEO, Micro Arc Oxidation, MAO, SEM, Titanium alloy, NiTi