<abstract xmlns="http://www.w3.org/1999/xhtml">Acid dissolution of soda-lime glass was rigorously investigated. Aqueous solutions containing 1N HNO3, HCl, H2SO4 and CH3COOH were used to measure the durability of the soda-lime glass samples. Flame emission spectrometry (FES) and UV-visible absorption spectroscopy were used to determine the concentration of Na+, K+, Ca2+ and Si4+ ions in solutions after dissolution. Weight loss analyses and microstructural characterization were used to evaluate the compositional changes of the glass samples.</abstract>

Acid dissolution of soda-lime glass was rigorously investigated. Aqueous solutions containing 1N HNO3, HCl, H2SO4 and CH3COOH were used to measure the durability of the soda-lime glass samples. Flame emission spectrometry (FES) and UV-visible absorption spectroscopy were used to determine the concentration of Na+, K+, Ca2+ and Si4+ ions in solutions after dissolution. Weight loss analyses and microstructural characterization were used to evaluate the compositional changes of the glass samples.

Chemical durability of soda-lime glass in aqueous acid solutions

Department of Chemistry and Chemical Engineering, Ovidius University of Constanta, 124 Mamaia Blvd, 900527 Constanta, Romania

Pedological and Agrochemical Studies Office,17-19 Revolutiei Street, 900735 Constanta, Romania

Ovidius University Annals of Chemistry

{"article-title":"Chemical durability of soda-lime glass in aqueous acid solutions"}

Acid dissolution of soda-lime glass was rigorously investigated. Aqueous solutions containing 1N HNO3, HCl, H2SO4 and CH3COOH were used to measure the...

Chemical durability of soda-lime glass in aqueous acid solutions

Published Online: Mar 22, 2013

Page range: 128 - 132

DOI: https://doi.org/10.2478/v10310-012-0021-6

Keywords
glass, chemical durability, silicates

This content is open access.

Chemical durability of soda-lime glass in aqueous acid solutions

Published Online: Mar 22, 2013

Page range: 128 - 132

DOI: https://doi.org/10.2478/v10310-012-0021-6

Keywordsglass, chemical durability, silicates

This content is open access.

Keywords
glass, chemical durability, silicates