1 | In situ (B) | 8 | orSi | UUC | 24.2 | 70%/h | 18.9 |
2 | In situ (B) | 9 | orSi | UUC | 27.3 | 70%/h | 21.3 |
3 | In situ (B) | 10 | orSi | UUC | 28.2 | 70%/h | 22.1 |
4 | In situ (B) | 10 | orSi | UUC | 29.3 | 70%/h | 22.9 |
5 | In situ (N/A) | 8.5 | orSi | FVT | 30.7(2) | 0.1°/s (700%/h) | 30.7(2) |
6 | In situ (N/A) | 9 | orSi | FVT | 30.1(2) | 0.1°/s (700%/h) | 30.1(2) |
7 | In situ (N/A) | 9 | orSi | FVT | 28.5(2) | 0.1°/s (700%/h) | 28.5(2) |
8 | In situ (N/A) | 10 | orSi | FVT | 33.5(2) | 0.1°/s (700%/h) | 33.5(2) |
9 | Reconstituted (A) | 9 | orSi | CK0UC | 32.7 | 1%/h | 32.7 |
10 | Reconstituted (A) | 9 | orSi | CK0UC | 29.3 | 1%/h | 29.3 |
11 | Reconstituted (A) | 9 | orSi | DSS | 27.2 | 20%/h | 22.8 |
12 | Reconstituted (A) | 9 | orSi | DSS | 29.3 | 20%/h | 24.5 |
4 | 2949 | 2679 | 0.239 | 0.215 | 1.196 | 0.283 | 18.4 |
5 | 3311 | 3058 | 0.213 | 0.203 | 1.216 | 0.269 | 26.3 |
9 | 3125 | 2905 | 0.243 | 0.291 | 1.189 | 0.288 | 18.6 |
AVG | 3128 | 2881 | 0.232 | 0.236 | - | - | - |
SD | 147 | 155 | 0.013 | 0.039 | - | - | - |
COV | 0.05 | 0.05 | 0.06 | 0.16 | - | - | - |
1 | 1468 | 1304 | 0.601 | 0.557 | 0.973 | 0.511 | 14.9 |
2 | 1342 | 1125 | 0.788 | 0.687 | 0.811 | 0.783 | 0.5 |
3 | 1565 | 1351 | 0.525 | 0.434 | 1.037 | 0.432 | 17.7 |
6 | 983 | 843 | 1.141 | 1.077 | 0.728 | 0.976 | 14.4 |
7 | 1175 | 973 | 0.951 | 0.816 | 0.673 | 1.127 | 18.6 |
8 | 1462 | 1240 | 0.583 | 0.536 | 0.982 | 0.499 | 14.4 |
AVG | 1332 | 1140 | 0.764 | 0.684 | - | - | - |
SD | 198 | 181 | 0.221 | 0.213 | - | - | - |
COV | 0.14 | 0.16 | 0.29 | 0.31 | - | - | - |
1 | O3 | 10.5–11 | 24h IL | 50.6 | 1.46 | 2.58 | Sample few cm to no.2 |
O3 | 10.5–11 | 24h IL | 59.9 | 1.29 | 2.58 | Sample few cm to no.1 | |
3 | O1 | 9.5–10 | 24h IL | 51.4 | 1.57 | 2.57 | O1 borehole is at distance of 10 m from O2 |
4 | O2 | 9.5–10 | 24h IL | 42.9 | 1.71 | 2.54 | O2 borehole is at distance of 10 m from O1 |
5 | O3 | 9.3–9.8 | 24h IL | 48.0 | 1.80 | 2.58 | |
6 | O3 | 10–10.5 | 24h IL | 91.0 | 1.39 | 2.46 | Very variable water content and plasticity of soil in the tube |
7 | O4 | 10–10.5 | 24h IL | 103.5 | 1.37 | 2.26 | Very variable water content and plasticity of soil in the tube |
8 | O4 | 10.5–11 | 24h IL | 55.8 | 1.53 | 2.52 | - |
9 | O2 | 9.5–10 | CRS* | 41.2 | 1.68 | 2.57 | - |
LOI | 10%<LOI<30% | 5%<LOI<10% | LOI>30% | ASTM D2974 or PN-ISO 10694 |
Fines | ~50% of Cl and Si | ~95% of Si | N/A | Laser diffraction method |
wc | 63.5±21.0 | 45.5±18.5 | 261±110.4 | ASTM D2216 or PN-EN ISO 17892-1 |
ρ | 1.58±0.16 | 1.74±0.18 | 1.17±0.27 | ASTM D854 or PN-EN ISO 17892-2 |
Gs | 2.61±0.06 | 2.60±0.06 | 2.04±0.32 | ASTM D7263 or PN-EN ISO 17892-3 |
LL | 82.5±32.1 | 52.0±21.0 | 268.9±115.7 | ASTM D4318 or PN-EN ISO 17892-12 |
IP | 50.1±25.1 | 29.4±13.8 | 159.4±87.5 | ASTM D4318 or PN-EN ISO 17892-12 |
Casagrande's chart | Along and above A-line | Above A-line | N/A | ASTM D2487 or PN-EN ISO 14688-2 |
1 | In situ (D) | 9–10 | orSi | CK0UC | 26.4 | 1%/h |
2 | In situ (D) | 9–10 | orSi | CK0UC | 32.7 | 1%/h |
4 | N/A | 9–10 | orSi | SHANSEP | 25±5.2 | N/A |
<1 | A | <0.04 | <0.03 | v. good to excellent (A) | <0.15 | High |
1–2 | B | 0.04–0.07 | 0.03–0.05 | good to fair (B) | 0.15–0.4 | Moderate |
2–4 | C | 0.07–0.14 | 0.05–0.1 | Poor (C) | >0.4 | Low |
4–8 | D | >0.14 | >0.1 | Very poor (D) | - | - |
>8 | E | - | - | - | - | - |
1 | In situ (D) |
2–3 | orCl | CK0UC | 17.0 | 1%/h |
2 | In situ (D) |
2–3 | orCl | CK0UC | 23.4 | 1%/h |
3 | In situ (D) |
2–3 | orCl | CK0UE | 15.2 | 1%/h |
4 | N/A | 2–3 | orCl | SHANSEP | 18.2±9.5 | N/A |