Sintering of titanate based dielectrics doped with lithium fluoride and calcium borosilicate glass

Published Online: 03 Aug 2011
Volume & Issue: Volume 29 (2011) - Issue 1 (March 2011)
Page range: 29 - 34
Journal Details
License
Format
Journal
eISSN
2083-134X
ISSN
2083-1331
First Published
16 Apr 2011
Publication timeframe
4 times per year
Languages
English
Abstract

The effect of LiF and CBS glass additives on the microstructure and dielectric property of BaTiO3 (BT) ceramics was studied. The phase of BaLiF3 was observed from the interaction between BT and LiF when the samples were sintered at 900 °C for 1 h. Crystal grains with Ba and F in atomic ratios of 1:3 were observed from the SEM and TEM analysis of the microstructures. Abnormal grain growth (AGG) was observed to occur in the BT ceramics sintered at 950 °C. Further improvement to the composition was achieved by employing a two-stage process. This included CBS glass shell coating of the BT particles in the first stage, and the addition of LiF in the second stage. The composition thus formed had very good permittivity (1725) and an extremely low dielectric loss value (0.008).

Keywords

[1] Jeon H.P., Lee S.K., Kim S.W., Chi D.K., Mater. Chem. Phys., 94 (2005), 185. http://dx.doi.org/10.1016/j.matchemphys.2005.04.04910.1016/j.matchemphys.2005.04.049Search in Google Scholar

[2] Lin Y.S., Liu C.C., Li K.M, Chen C.H, IEEE Trans. Microwave Theory and Techn., 52 (2004) 2718. http://dx.doi.org/10.1109/TMTT.2004.83829210.1109/TMTT.2004.838292Search in Google Scholar

[3] Baker A., Lanagan M., Randall C., Semouchkina E., Semouchkin G., Rajah K.Z., Eitel R., Rajab K.Z., Mittra R., Rhee S., Int. J. Appl. Ceram. Technol., 2 (2005) 514. http://dx.doi.org/10.1111/j.1744-7402.2005.02052.x10.1111/j.1744-7402.2005.02052.xSearch in Google Scholar

[4] Hirata A., Yamaguchi T., J. Am. Ceram. Soc., 80 (1997), 79. http://dx.doi.org/10.1111/j.1151-2916.1997.tb02793.x10.1111/j.1151-2916.1997.tb02793.xSearch in Google Scholar

[5] Hsiang H.I., Hsi C.S., Huang C.C., Fu S.L., Mater. Chem. Phys., 113 (2009), 658. http://dx.doi.org/10.1016/j.matchemphys.2008.08.03310.1016/j.matchemphys.2008.08.033Search in Google Scholar

[6] Hsiang H.I., Hsi C.S., Huang C.C., Fu S.L., J. Alloy. Compd., 459 (2008), 307. http://dx.doi.org/10.1016/j.jallcom.2007.04.21810.1016/j.jallcom.2007.04.218Search in Google Scholar

[7] Walker Jr. B.E., Rice R.W., Pohanka R.C., Spann J.R., Am. Ceram. Soc. Bull., 55 (1976), 274. Search in Google Scholar

[8] Lin, J.N., Wu, T.B., J. Am. Ceram. Soc., 72 (1989), 1709. http://dx.doi.org/10.1111/j.1151-2916.1989.tb06307.x10.1111/j.1151-2916.1989.tb06307.xSearch in Google Scholar

[9] Ruiz-Valdés J.J., Gorokhovsky A.V., Escalante-Garcí A J.I., Mendoza-Suarez, J. Europ. Ceram. Soc., 24 (2004), 1508. http://dx.doi.org/10.1016/S0955-2219(03)00531-410.1016/S0955-2219(03)00531-4Search in Google Scholar

[10] Lee J.A., Lee J.H., Kim J.J., J. Europ. Ceram. Soc., 26 (2006), 2135. http://dx.doi.org/10.1016/j.jeurceramsoc.2005.09.08110.1016/j.jeurceramsoc.2005.09.081Search in Google Scholar

[11] Hsi C.S., Chen Y.C., Jantunen H., Wu M.J., Lin T.C., J. Euro. Ceram. Soc., 28 (2008), 2581. http://dx.doi.org/10.1016/j.jeurceramsoc.2008.03.01410.1016/j.jeurceramsoc.2008.03.014Search in Google Scholar

[12] Lin T.C., Under-graduate project report, National United University, Taiwan, 2006. Search in Google Scholar

Recommended articles from Trend MD

Plan your remote conference with Sciendo