This study examines the influence of SiO2 and Na2O mix proportions on the properties of alkali-activated slag (AAS) pastes. In order to solve the rapid setting problem associated with AAS, phosphoric or silicic acid is commonly added to the alkaline activator. The retarding effect of these additions suggests a close relationship between pH and setting time. In this study, AAS pastes with various SiO2 and Na2O dosages were analyzed. Regression analysis was carried out using pH value and setting time to identify the main parameters affecting the setting time. Results showed that the alkali modulus (i.e., the weight ratio of SiO2 over Na2O) is correlated with the pH value. Specifically, the initial and final setting times were significantly reduced under lower SiO2 and Na2O dosages. Therefore, a higher alkali modulus prolonged the setting time.
</abstract>

This study examines the influence of SiO2 and Na2O mix proportions on the properties of alkali-activated slag (AAS) pastes. In order to solve the rapid setting problem associated with AAS, phosphoric or silicic acid is commonly added to the alkaline activator. The retarding effect of these additions suggests a close relationship between pH and setting time. In this study, AAS pastes with various SiO2 and Na2O dosages were analyzed. Regression analysis was carried out using pH value and setting time to identify the main parameters affecting the setting time. Results showed that the alkali modulus (i.e., the weight ratio of SiO2 over Na2O) is correlated with the pH value. Specifically, the initial and final setting times were significantly reduced under lower SiO2 and Na2O dosages. Therefore, a higher alkali modulus prolonged the setting time.

Delayed setting time for alkali-activated slag composites using activator containing SiO2 and Na2O

Department of Harbor and River Engineering

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Delayed setting time for alkali-activated slag composites using activator containing SiO and NaO

This study examines the influence of SiO2 and Na2O mix proportions on the properties of alkali-activated slag (AAS) pastes. In order to solve the rapid setting...

Delayed setting time for alkali-activated slag composites using activator containing SiO₂ and Na₂O

Published Online: Apr 26, 2022

Page range: 570 - 579

Received: Jan 07, 2022

Accepted: Mar 06, 2022

DOI: https://doi.org/10.2478/msp-2021-0045

Keywords
alkali-activated materials, setting time, silicate-based activator, microstructures

© 2021 Chi-Che Hung et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Delayed setting time for alkali-activated slag composites using activator containing SiO2 and Na2O

Published Online: Apr 26, 2022

Page range: 570 - 579

Received: Jan 07, 2022

Accepted: Mar 06, 2022

DOI: https://doi.org/10.2478/msp-2021-0045

Keywordsalkali-activated materials, setting time, silicate-based activator, microstructures

© 2021 Chi-Che Hung et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Delayed setting time for alkali-activated slag composites using activator containing SiO₂ and Na₂O

Keywords
alkali-activated materials, setting time, silicate-based activator, microstructures